7-Octenyltrimethoxysilane, a model coupling molecule to study the adhesion promotion of a silicone elastomer on an Al 2024 alloy

Help me understand this report

Search citation statements

Order By: Relevance

Paper Sections

Select...
1
1
1
1

Citation Types

0
4
0

Year Published

2009
2009
2022
2022

Publication Types

Select...
9

Relationship

0
9

Authors

Journals

citations
Cited by 27 publications
(4 citation statements)
references
References 42 publications
0
4
0
Order By: Relevance
“…The adhesion test of the coating is carried out by method B – orthogonal notch tape test in ASTM D3359. 34–40 After spraying the coating evenly on the surface of the glass substrate, the sample was placed on a horizontal platform. The coating surface was cut with a cutting tool at a cutting speed of (15–25) mm s −1 to make 6 strips in the axial and longitudinal directions of the glass substrate, respectively.…”
Section: Methodsmentioning
confidence: 99%
“…The adhesion test of the coating is carried out by method B – orthogonal notch tape test in ASTM D3359. 34–40 After spraying the coating evenly on the surface of the glass substrate, the sample was placed on a horizontal platform. The coating surface was cut with a cutting tool at a cutting speed of (15–25) mm s −1 to make 6 strips in the axial and longitudinal directions of the glass substrate, respectively.…”
Section: Methodsmentioning
confidence: 99%
“…Fig. 9a and b is the fitted Al2p and O1s spectra for the sample immersed in the solution without inhibitor for 0.5 h. On the Al2p spectra three Al peaks are seen at 71.8 eV, 74.1 eV and 75.2 eV, which may be assigned to metallic aluminum [31], Al 2 O 3 [32] and Al(OH) 3 [32] respectively. On the O1s spectra also three Table 4 EIS fitting parameters as a function of immersion time in 0.58 g L −1 NaCl solution (pH 10) with different inhibitors.…”
Section: Eis Analysismentioning
confidence: 99%
“…It has multifunctional groups with a general chemical formula of R-SiX 3 , where X stands for hydrolysable groups bonded to Si atoms, and R is a resin-compatible group. It is commonly used to significantly increase the bond strength and durability by providing the chemical bridge to connect the inorganic material (especially silicon-containing materials) and resin [2][3][4]. By using the right silane coupling agent, a poorly adhering paint, ink, coating, adhesive or sealant can be converted to a material that often will maintain adhesion even if subjected to severe environmental conditions.…”
Section: Effect Of the Adhesion Promoter On The Adhesion Strengthmentioning
confidence: 99%