Aim: To investigate push-out bond strength (PBS) of fiber post to radicular dentin after using different cementation techniques. Material and methods: Sixty single-rooted premolars were disinfected and cleaned by mechanical instrumentation. S1, S2, and SX were used for canal shaping and finishing of the canal was carried out using F1 and F2. This was followed by constant irrigation and smear layer removal using 17%EDTA. The canal was dried filled with gutta-percha and canal space was prepared using a peso reamer. Based on cementation techniques, samples were randomly allocated into six groups. Group 1: One-step Monoblock MC; Group 2: One-step, Monoblock MC-NA (no adhesive) GFP; Group 3: One-step, RX-MC-Monoblock; Group 4: Two-step, RX-MC; Group 5: Two-step, RX-FZ; and Group 6: Two-step RX-FZ-custom post. All specimens were mounted in polyvinyl pipes using acrylic resin up to cement enamel junction. All specimens were mounted in a universal testing machine subjected to push-out forces at a speed of 0.5 mm/min. Five samples from each group were sputter-coated with 6 nm gold thickness for 300 s at 250 mA. The coated specimens were assessed under the scanning electron microscope (SEM). Analysis of variance (ANOVA) and Tukey Kramer multiple comparisons tests were performed to compare means among groups maintaining the level of significance at ( p < 0.001). Results: The highest PBS was displayed in RX-MC-Monoblock (199.020 ± 21.432 MPa). Whereas, lowest PBS was found in Monoblock MC-NA (no adhesive)-GFP (76.440 ± 9.468 MPa). Among one-step groups, RX-MC Monoblock exhibited the highest PBS (199.020 ± 21.432 MPa) comparable to one-step Monoblock MC (134.28 ± 19.37 MPa) ( p > 0.05). Similarly, among two-steps groups, two-step RX-MC demonstrated significantly higher PBS values than two-step RX-FZ (143.340 ± 23.68 MPa) and RX-FZ-custom post (86.90 ± 7.41 MPa) ( p < 0.05). Conclusion: One-step RX-MC-Monoblock technique using self-adhesive cement and core foundation composite resin material multicore flow when cured simultaneously exhibited the highest bond integrity of post retention compared to other cementation technique.