The Gibbs energy of formation of the solution and compound phases in the Al‐Nb‐Ti system were derived from an optimisation procedure using all the available experimental thermodynamic and phase diagram data. The thermodynamic description of the ordered compounds was made using a multi‐sublattice model, while a Redlich‐Kister polynomial was used for the solution phases.