A pH-Sensitive Lignin-Based Material for Sustained Release of 8-Hydroxyquinoline

Abstract

The fabrication of pH-sensitive lignin-based materials has received considerable attention in various fields, such as biomass refining, pharmaceuticals, and detecting techniques. However, the pH-sensitive mechanism of these materials is usually depending on the hydroxyl or carboxyl content in the lignin structure, which hinders the further development of these smart materials. Here, a pH-sensitive lignin-based polymer with a novel pH-sensitive mechanism was constructed by establishing ester bonds between lignin and the active molecular 8-hydroxyquinoline (8HQ). The structure of the produced pH-sensitive lignin-based polymer was comprehensively characterized. The substituted degree of 8HQ was tested up to 46.6% sensitivity, and the sustained release performance of 8HQ was confirmed by the dialysis method, the sensitivity of which was found to be 60 times slower compared with the physical mixed sample. Moreover, the obtained pH-sensitive lignin-based polymer showed an excellent pH sensitivity, and the released amount of 8HQ under an alkaline condition (pH = 8) was obviously higher than that under an acidic condition (pH = 3 and 5). This work provides a new paradigm for the high-value utilization of lignin and a theory guidance for the fabrication of novel pH-sensitive lignin-based polymers.

Lignins as Promising Renewable Biopolymers and Bioactive Compounds for High-Performance Materials

“…A novel pH-sensitive material was obtained by incorporation of ester bonds between lignin and 8-hydroxyquinoline (8HQ). The pH sensitivity and the sustained amount of 8HQ released under alkaline conditions (pH = 8) was higher than that under acidic conditions (pH = 3 and 5) [142]. Alkali lignin, as an ionotropic crosslinker, has been used to obtain chitosan-alkali lignin thermo-responsive hydrogels [143] for wound-dressing applications.…”