A Study of the Performance of Dissimilar Pulsed-Laser-Welded JSC590R/JAC980YL Steel Joints of Differential Thickness

Abstract

To reveal the correlation between the mechanical properties of JSC590R/JSC980YL steel pulse-laser-welded joints and welding parameters, this study adopts the response surface analysis test method to determine the welding parameters, and examined the macroscopic morphology, microstructure, microhardness, and tensile properties of the cross-section of the welded joints. The results revealed that the key factors influencing welded joints quality, in descending order of importance, are distance to focus, welding speed, and single-pass heat input. The interaction between these factors is extremely significant. The weld zone of the joints is primarily composed of lath martensite, while the heat-affected zone is composed of ferrite, martensite, carburite, tempered martensite, and residual austenite. The optimized welding parameters align with actual expectations, yielding an average engineering stress of 616.9 MPa for the joint. Notably, the fracture area shifts from the heat-affected zone of JSC590R to the base material.