A Study on Friction-induced Surface Fracture Behaviors of Carboxylic Acid Modified Styrenic Thermoplastic Elastomer as Additives

Abstract

또는 아연이온이 코팅된 실리카를 첨가한 m-TPS는 zinc ion과 carboxylic acid group 간의 ionic cluster 형성을 통하여 기계적 강도, 내마모성과 마찰 시 표면 파괴가 개선되었다. Zinc ion과 carboxylic acid group 간의 ionic cluster 형성은 1550~1650cm -1 의 zinc carboxylate group stretch 피크의 FT-IR 분석 결과로 확인하 였다. Abstract:In this work, we observed the effect of silica, zinc oxide, zinc ion coated silica on carboxylic acid modified styrenic thermoplastic elastomer (m-TPS) film for friction-induced surface fracture. m-TPS film added general silica showed poor mechanical properties, anti-abrasion and friction-induced surface fracture, caused by strong filler-filler interaction of silica. In case of m-TPS films added zinc oxide or zinc ion coated silica, mechanical properties, anti-abrasion and friction-induced surface fracture were improved due to forming ionic cluster between carboxylic acid group of m-TPS and zinc ion. Ionic cluster were confirmed by FT-IR analysis that observed zinc carboxylated group stretch peak at 1550~1650 cm -1 .