Adhesion and interfacial reactions on metal/oxide interface during plastic deformation at room temperature

Abstract

Properties of interfaces in solid state metal/oxide joints (Al/SiO 2 , Al/MgO, Al/glass, Mg/MgO, Mg/SiO 2 , In/glass etc.) are reported. The interfaces were formed at plastic deformation of metal on the oxide surface at room temperature. Their structure, chemical composition, and micromechanical properties were studied by the AFM, XRD, SIMS, optical microscopy, and precision microindentation techniques. A noticeable adhesion was observed for metals with high affinity for oxygen and only in the regions of the maximum shear stress. Formation of an interfacial reaction zone with an oxygen concentration gradient is detected. In this zone metals are nanostructured and noticeably hardened. The effect of mechanoactivation is considered as a result of physical and chemical interaction and formation of nanostructures in deformed metal/oxide systems.Key words: metal/oxide interfaces, adhesion, interfacial reaction, mechanoactivation, nanostructure.