Biodegradable Chitosan-Based Membranes for Highly Effective Separation of Emulsified Oil/Water

Abstract

Efficient separation of oil droplets from oil/water emulsions is necessary for many energy and food industrial processes and for industrial wastewater treatment. Membrane microfiltration has been explored to address this issue because it is simple to operate and low in cost. However, filtration of oil droplets with a size around or less than 1 μm is still a major challenge. Furthermore, the fabrication process for polymeric membranes often uses hazardous organic solvents and petroleum-derived and nonbiodegradable raw materials, which pose additional environmental health and safety risk. In this study, we examined the use of chitosan-based membranes to efficiently remove oil droplets with an average diameter of ∼1 μm. The membranes were fabricated based on the rapid dissolution of chitosan in an alkaline/urea solvent system at a low temperature, thus avoiding the use of any toxic organic solvent. The chitosan membranes were further modified by dopamine and tannic acid (TA). The as-prepared membrane was characterized in terms of surface morphology, pore size distribution, and mechanical strength. The membrane performance was evaluated on a custom-designed crossflow filtration system. The results showed that the modified chitosan membrane with dopamine and TA had a water flux of 230.9 LMH at 1bar transmembrane pressure and oil droplet rejection of 99%. This water flux represented an increase of more than 10 times when compared with the original chitosan membrane without modification. The study also demonstrated excellent antifouling properties of the modified membrane that could achieve near 100% water flux recovery.

Karakteristik Sifat Fisik Membran Elektrolit Polimer Berbasis Kitosan Larva Black Soldier Fly/Polivinil Alkohol/Poliakrilonitril dengan Penambahan Ammonium Klorida

“…Nilai densitas tertinggi sebesar 1,510 g/mL pada komposisi PVA/PAN 10:90 dan kitosan 3,2 g. Sementara itu, nilai densitas terendah sebesar 0,734 g/mL pada komposisi PVA/PAN 20:80 dan kitosan 2,4 g. Hasil yang diperoleh menunjukkan bahwa nilai densitas mengalami peningkatan dengan penambahan kitosan yang meningkat. Dengan bertambahnya komposisi kitosan, kerapatan membran yang dihasilkan juga meningkat [22]. Gambar 2 juga menunjukkan nilai densitas pada komposisi PVA/PAN 20:80 yang memiliki nilai densitas yang lebih rendah dibandingkan komposisi PVA/PAN 10:90.…”