Bulge test technique and digital image correlation for the determination of the biaxial behavior of polymeric films

Abstract

Materials can display multiple mechanical behaviors when they are biaxially stressed. In this research work, films obtained through the blowing process were investigated in order to compare the mechanical properties and behavior of the film under uniaxial and biaxial stress conditions. Bulge test coupled with a continuous full-field strain measurement was undertaken in order to characterize polymeric film in a biaxial stress state. As far as this study is concerned, a laboratory-made pneumatic bulge test machine was used for the determination of the biaxial behavior of a 50 μm thickness PLSF (modified PLA) film. 3D-digital image correlation (3D-DIC) technique was used in order to compute the strain field continuously during the test. Tensile test was equally performed on the film along its machine direction (MD) and transverse direction (TD). Strain field distribution in the film sample was analyzed and compared in both tests. The tensile test results displayed an isotropic behavior of the film in both directions. However, a difference in the strain at break was noticed because of the thickness instability along the TD. The comparison between uniaxial and biaxial properties resulted in almost the same properties with respect to the Young Modulus as well as the tensile strength.