Comparative Study of Architectural Bricks from Khorsabad and Susa Sites: Characterization of Black Glazes

Abstract

In this study, the well-preserved glazes of 13 colored bricks representative of the decoration of the palaces of Sargon II (Khorsabad, 8th century BC) and of Darius I (Susa, 6th century BC) were examined. The purpose of this research is to gather information about the ancient brick manufacturing processes by examining the colored glazes and, in particular, black glazes using a combination of methods that included optical microscopy, SEM-EDX, synchrotron µ-XRD, and µ-Raman spectroscopy. The results revealed different coloring techniques for producing black glazes in the Neo-Assyrian and Persian Achaemenid periods. Regarding the black glazes of Susa, it is particularly interesting to note that their chemical composition varies according to the function of the glazes on the bricks: manganese oxide (for colored fields of glaze) and iron-rich compounds (for raised lines separating glazed areas). In comparison, the black glazes from Khorsabad are characterized by the presence of spherical copper sulfide and galena nanoparticles (ranging from less than 100 nm to about 1 µm) for both the glazed areas and the separating lines. This coloring technique to obtain black glazes is very rarely described in the literature, as well as the mechanism of formation of these spherical nanoparticles.

An Archaeometric Study of Lead-Glazed Medieval Ceramics (13th–14th Century) from Santarém, Portugal

“…Some authors [39][40][41] referred to the use of Sb-based opacifiers in the studied glazes (from Korchabad, Susa, Persepolis, and Tepe Rabat-8th and 6th centuries BC), present as lead antimonate, calcium antimonate, and/or sodium antimonate. In some cases [39], even no Pb was detected.…”