CORROSION BEHAVIOUR OF TEMPERED 42CrMo4 STEEL

Abstract

Low-alloy 42CrMo4 steel (AISI 4140) is a medium carbon steel, commonly used as a quenched and tempered steel. Because of its good mechanical properties, high tensile strength and toughness, 42CrMo4 is one of the widely used and investigated steels. In order to increase ductility even more, in addition to standard quenching and tempering, steel is often hardened by double quenching and tempering and austempering. The aim of this paper was to investigate the corrosion behaviour of 42CrMo4 steel after quenching and tempering, double quenching and tempering and austempering. For this purpose, microstructural characterization and electrochemical investigation after different hardening processes were performed. Microstructure of specimens was observed using optical microscopy and scanning electron microscopy. Open circuit potential and potentiodynamic polarization measurements of tempered specimens were carried out using computer-controlled potentiostat with three electrode set-up in 0.6 M NaCl naturally aerated solution. It was concluded that applied heat treatment processes increase the corrosion resistance of 42CrMo4 steel in comparison to normalized steel. In comparison to quenched and tempered steel, double quenching and tempering, as well as austempering, do not significantly change corrosion resistance of steel.

Ex‐Situ Synchrotron X‐Ray Diffraction Study of Co2 Corrosion‐Induced Surface Scales Developed in Low‐Alloy Steel with Different Initial Microstructure

“…1 and 5a. The high reactivity caused by the lath martensitic structures and the presence of high dislocation density are also reported in the previous works related to martensitic and tempered martensitic structures 4 [18,48,49]. As a result, the QT sample dissolves more Fe ions compared to the FC sample.…”