Cutting Stone Building Materials With Cut Wheels of Cubic Boron Nitride

Abstract

The advantage of cutting stone building materials with SSM (synthetic superhard materials) wheels is that, first of all, it is possible to obtain high processing productivity and dimensional stability, which are 3..5 and 50…100 times higher than those of traditional tools based on carborundum, respectively. The study of the process of cutting stone materials with CBN (cubic boron nitrite) wheels is aimed at establishing force dependences, determining the cutting power and heating temperature of the cutting disc during operation. The forces were measured using a tensometric dynamometer UDM-50. To measure and calculate the cutting temperature, a thermoelectric method based on the formation of practically not inertial microthermocouples during cutting was used. The temperature to which the CBN cutting wheel on a metal base is heated is a limiting factor in processing, since when heated to a temperature of 600ºС, the strength of the wheel decreases by half, which can cause its rupture under the action of centrifugal forces, as well as loss of stability and jamming during cutting. In the present study, the wheel temperature was measured after one minute of continuous operation. The values of the component of the cutting force PY, depending on the processing modes, can reach values of the order of 70 N. The values of the component of the cutting force PZ, depending on the processing modes, can reach values of 45 N. The cutting power can be 2800W. The temperature resistance of the wheel (heating time of the wheel up to 600ºС) when cutting dry is maximum 28 minutes, when grinding with cooling of the cutting zone with negative temperature air from a Ranque-Hilsch tube, the temperature resistance is 35 minutes, with ejector cooling of sprayed coolant 37 minutes and with jet-pressure cooling it is 40 minutes. The maximum cutting length is respectively 0.7: 0.8; 0.9 and 2m. The cutting power is 600...2800W.