Effect of heat treatment on Charpy impact energy of microalloyed steel

Abstract

Original scientific paper In this paper the microalloyed high-strength low-alloy (HSLA) Niomol 490K steel with an addition of niobium (0,032 wt. %) has been investigated. Heat treatment of the steel consisted of austenitisation at 1250 °C for 3 minutes and reheating up to 750 °C for 5 s. After austenitization the quenching was carried out in water with temperature of 70 °C and then in a lead bath up to 400 °C following cooling on the air. It was found that Charpy impact energy is higher and the transition temperature is lower for the transformation of austenite to bainite than to martensite microstructure. Experimental results showed that different fracture surface was observed. It is shown that preferred cleavage fracture occurred in the lattice plane (001) Utjecaj toplinske obrade na Charpy energiju udara mikrolegiranog čelikaIzvorni znanstveni rad U ovom radu istraživan je niskolegirani visokočvrsti čelik Niomol 490K koji sadrži dodatak niobija (0,032 mas. %). Toplinska obrada čelika se sastojala od austenitizacije pri 1250 °C u trajanju od 5 minuta i ponovnog zagrijavanja do 750 °C u trajanju od 5 s. Nakon austenitizacije provedeno je kaljenje u vodi kod temperature od 70 °C i u olovnoj kupci do temperature od 400 °C uz naknadno hlađenje na zraku. Utvrđeno je da je Charpy energija udara viša, a prijelazna temperatura niža za transformaciju austenita u bainit nego kod transformacije austenita u martenzitnu mikrostrukturu. Eksperimentalni rezultati su pokazali različite prijelomne površine. Pokazano je da je preferentno cijepajući prijelom zapažen po ravnini rešetke (001), neovisno o mikrostrukturi.