Effect of Hot Deformation Temperature on Texture Formation Regularity of CGO Silicon Steel under High Deformation Rate

Abstract

The influence of hot deformation temperature on microstructure and texture of CGO silicon steel under the condition of a high deformation rate (100 s-1) was studied by SEM and EBSD techniques. The results indicate that the typical microstructures at room temperature consist of ferrite and pearlite under different hot deformation temperatures. The higher deformation temperature is beneficial to obtain a more uniform recrystallization microstructure and lower pearlite content. Cubic texture{100}001and rotated cubic texture{100}011are dominant texture components in the tested steels, and{111}112texture inγfiber is also strong, the intensity of which is higher than that of{111}110texture. Goss texture{110}001is weak. With the rising of the hot deformation temperature,{100}011texture decreases firstly and then increases at 1100°C. When the hot deformation temperature raises from 800°C to 900°C,{111}112texture shows an increasing trend, while{111}110texture content is stable. When the temperature further increases to 1100°C and 1150°C,{111}112and{111}110textures are slightly weakened.