Effect of Initial Microstructure on the Temperature Dependence of the Flow Stress and Deformation Microstructure under Uniaxial Compression of Ti-407

Abstract

In this study, the influence of initial microstructure and deformation temperature on the flow stress behavior and microstructural evolution of TIMETAL®407 (Ti-407) alloy are investigated. For this purpose, compression cylinders were β-annealed at 940 °C and then cooled to room temperature using furnace cooling, static air, and water quenching to promote three initial microstructures with different α lath thicknesses. The annealed cylinders were compressed isothermally in the range of 750 °C to 910 °C at a constant crosshead speed of 0.05 mm/s up to an engineering strain of −0.8. The resulting stress–strain curves are discussed in terms of the morphology and distribution of the α and β phases. It was found that flow stress is inversely proportional to deformation temperature for all initial microstructures. At the lowest temperatures, compressive yield strength was higher in water-quenched and air-cooled samples than in furnace-cooled specimens, suggesting that the acicular α-phase morphology obtained by rapid cooling could enhance mechanical strength by hindering dislocation motion. Two high-temperature flow regimes were determined based on the shape of the flow stress curves, indicating microstructural changes occurring during deformation. At higher temperatures, the effect of the initial microstructure is negligible as the primary α phase is transformed to the β phase at around 850 °C irrespective of the initial α-lath thickness.