Effect of Surface Roughness on Corrosion Resistance of Mooring Chains for Offshore Floating Photovoltaics

Abstract

Mooring chains are key components of offshore floating photovoltaic systems. Although their service safety is often affected by the harsh service environment, the influence of surface roughness on their corrosion resistance is not clear. This study investigated the corrosion behavior of mooring chain steel using cyclic salt-spray corrosion and electrochemical tests. Scanning electron microscopy, energy-dispersive spectrometry, optical profilometry, and other analytical techniques were used to study the composition and morphology of the corrosion products. The corrosion behavior was studied by electrochemical polarization curves, alternating current impedance spectroscopy, and X-ray photoelectron spectroscopy. The results show that the salt-spray corrosion resistance of mooring chain steel significantly improved with the reduction in specimen surface roughness, and the number and depth of corrosion pits were reduced. Mass loss after 24 h of salt-spray corrosion was exponentially related to initial roughness (Ra). Improved surface roughness significantly increased the pitting potential of the specimens, widened the passivation range, and enhanced the repassivation capability, thus significantly improving the pitting resistance. The pitting potential is linearly related to the initial roughness of the specimen. The oxide contents of Fe, Mo, and Si in the passivation film tended to increase with a smoother surface, which contributes to its densification. This effectively blocks chloride ion attack, thus improving the corrosion resistance of the mooring chain steel.