Effect of Temperature and Acidity of Sulfuric Acid on Concrete Properties

Abstract

Concrete corrosion caused by sulphuric acid attack is a known phenomenon in sewer systems, resulting in significant economic losses and environmental problems. However, there is a scarcity of reported laboratory simulations and experimental work investigating the contributing factors controlling the corrosion. In this EPSRC (Engineering and Physical Sciences Research Council, UK) funded investigation the effect of temperature and the acidity of sulphuric acid solution on concrete specimens extracted from brand new concrete sewers has been investigated. In this investigation the concrete samples are submerged in three sulphuric acid solutions (pH = 0.5, 1 and 2) for 91 days under different temperatures (10ºC, 20ºC and 30ºC). Mass loss and compressive strength of the concrete specimens were tested and recorded at 7, 14, 28, 42, 56 and 91 days providing interesting data for visualising the changes taking place in the concrete samples (change in properties) during the time of immersion. The results revealed that samples overall mass increased at the early stages of the corrosion process. It also was observed that the overall mass of the samples decreased significantly at the later stages of the testing process with respect to the acidity of the solutions used. Although the change in temperature did not have a significant effect on the compressive strength of the tested samples , rise in temperature however, had considerable effect on the mass loss of the concrete samples which were immersed in the most aggressive solution (i.e., pH=0.5 and temperature = 30 o C) at 91 days. This research clearly demonstrated a high correlation between the acidity of the solution and the rate of corrosion with respect to time.

Modifying Mechanical Strength and Capillary Porosity of Portland Cement‐Based Mortar Using a Biosurfactant from Pseudomonas fluorescens

“…Lactobacillus (Firmicutes) was another abundant genus in the studied mortar samples, and some species of Lactobacillus can secrete biogenic organic acids to dissolve the cement paste matrix [43]. As acid products are formed, the hydration compounds (e.g., C-S-H, CaCO 3 , and Ca(OH) 2 ) of cement-based materials are eroded, and consequently, the materials gradually lose structure and decrease in compressive strength [49,55].…”

Efficient method of eliminating accidental damage of sewer tunnel

“…Studies of many domestic and foreign scientists are devoted to operation, repair and reconstruction of sewage tunnel collectors [4][5][6][7][8][9][10]. D. Stein [11], M. Mahmoodian [12], N.…”

Research and Selection of the Solution Composition for the Device of the Consolidated Part of the Restorable Sewerage Panel

“…Таким образом, первоочередной задачей коммунальных служб является обеспечение надежной работоспособности канализационных сетей. Следует отметить, что исследованию вопроса повышения эксплуатационной долговечности канализационных коллекторов посвящены многочисленные работы ученых Украины и зарубежных специалистов [1][2][3][4][5][6][7][8][9][10][11][12].…”