Effect Partial Substitution of Calcium by <i>Cadmium</i> on Dielectrically Properties of Li0.4Cd0.6Ba2Ca2Cu3O10+δ System

Abstract

In this article the conventional "solid-state reaction" method was used to synthesize perovskite Li0.4Cd0.6Ba2Ca2Cu3O10+δ. Four main types of compounds were obtained by physically replacing calcium oxide with cadmium in proportions 0, 0.03, 0.06 and 0.09, the pure Li0.4Cd0.6Ba2Ca2Cu3O10+δ phase, and the phases Li0.4Cd0.6Ba2Ca1.97Cd0.03Cu3O10+δ and Li0.4Cd0.6Ba2Ca1.94Cd0.06Cu3O10+δ and Li0.4Cd0.6Ba2Ca1.91Cd0.09Cu3O10+δ ,respectively from mixing their constituent oxides and pressed into pelts and then sintered in the furnace at 850 degrees Celsius for 90 hours: These samples have been studied for their original dielectrically properties. The real dielectric constant, dielectric loss factor, and tangent were calculated in the frequency range (50 to 1000000 HZ). It was found that the partial substitution of cadmium oxide plays an important role in enhancing dielectrically properties.