EMS-45 Tool Steels Hardenability Experiment using Jominy ASTM A255 Test Method

Abstract

Hardenability of steels is an important way to determine heat treatment and material properties that produce component products. Jominy test is one of the method to know hardenability of steels. The Jominy ASTM A255 in used as a method for carriying out and this reseach. Parameter such as austenite temperature, holding time, cooling rate and then the results is dedicated by the prediction result, with Non Linear Numerical Equation Method. Based on test, it's known, increasing austenite temperature, longer holding time and high cooling rate, will increase hardenability of steels. The different between the results and the prediction result done by Sonh Yue-Peng [15] , Matja equation [14] and Zehtab equation [10] , about 5 %-10 %. The data obtained from this experiment can be used to determine the appropriated heat treatment in order to get the desired mechanical properties, as well as to avoid distortion. Keywords Jominy, heat treatment, tool steels, distortion, hardenability AbstrakHardenability baja merupakan petunjuk penting untuk menentukan pola laku panas dan sifat bahan yang akan dilakukan dalam menghasilkan produk komponen. Salah satu cara untuk mengetahui hardenability baja, yaitu dengan menggunakan metode uji jominy. Penelitian ini, menggunakan metode uji jominy ASTM A255, dengan parameter temperatur austenisasi, waktu penahanan, media pendingin, kemudian diverifikasikan dengan hasil prediksi menggunakan metode persamaan numerik tidak linear. Berdasarkan hasil penelitian diperoleh, bahwa makin tinggi temperatur austenisasi dan makin lama waktu penahanan, nilai kekerasan akan semakin meningkat. Sedangkan untuk baja dengan laju pendiginan cepat kekerasannya lebih tinggi dibanding dengan baja pendinginan lambat. Perbedaan data hasil uji dan hasil prediksi yang dilakukan oleh Sonh Yue-Peng [5] , persamaan Matja [14] , dan persamaan Zehtab [10] , sekitar 5 %-10 %. Data dari hasil penelitian ini, dapat digunakan dalam penentuan laku panas yang sesuai dengan sifat mekanik yang diinginkan dan untuk menghindari terjadinya distorsi.

The Forecasting of the Effectve Thickness of a Tempered by High Frequency Current Layer for the “Reverse Idler Gear Shaft” Detail According to the 45 Steel Estimated Hardenability

“…Построение расчетных кривых прокаливаемости с применением метода ф. DS. Данный шаг оптимизирует построение кривых прокаливаемости, т. к. он исключает проведение по ГОСТ 5657-69 [16; 17] регламентированного испытания прокаливаемости стали методом торцовой закалки (по Джомини) [18][19][20]. Данный метод состоит в том, что один торец цилиндрического образца, нагретого до температуры закалки, охлаждают водой в специальной установке согласно ГОСТ 5657-69.…”