Experimental Study on the Crack Concrete Repaired via Enzyme-Induced Calcium Carbonate Precipitation (EICP)

Abstract

A low-carbon and environmentally friendly EICP method for repairing concrete cracks is presented to prolong the service life of concrete. In this study, we took concrete as the research object and quartz sand as the filling medium and employed the EICP injection method to repair concrete cracks. The internal repair effect of EICP on concrete cracks was evaluated with a combination of ultrasonic and compressive strength tests. The concrete repair mechanism of EICP was identified with a combination of EDS, XRD, and SEM tests. The results indicate that with an increase in the fracture depth, the ultrasonic sound time of the crack specimen increased gradually, and the ultrasonic wave transit time value of the crack specimen decreased significantly after EICP repair. After repair, the compressive strength rose. The highest compressive-strength recovery rate of a 0.3 mm wide specimen is 98.41%. The calcium carbonate crystal formed using EICP is vaterite. The probability density function model of the Laplace distribution was constructed, which showed good applicability and consistency in the ultrasonic sound time and compressive strength measured via experiments. The formed calcium carbonate crystals can be tightly and evenly attached to the cracks with the EICP injection repair method, resulting in a better repair effect.