Fabrication and Characterization Of Copper Doped Polymer/Bioactive Glass Composite Scaffolds

Abstract

Extended AbstractTissue damage and degenerative diseases such as large bone defects are among the most human health issues which lead to organ failure and death all over the world [1][2][3]. Bone tissue engineering emerges a promising approach to repair bone defects, especially large bone defects resulting from trauma, infections, tumors or genetic malformations [2][3][4]. The development of scaffolds and their processing into structures are becoming increasingly important in bone tissue engineering applications. Three-dimensional (3D) scaffolds should show a highly porous, open structure to allow a proper vascularisation of the implant, as well as the flow of nutrients and waste products through the scaffold. Major issues of bone tissue engineering scaffolds include the use of appropriate matrix materials for scaffolds, control of porosity and pore characteristics of scaffolds, mechanical strength of scaffolds as well as scaffold degradation properties [5]. Ideal bioactive porous scaffolds, which are used in bone tissue engineering applications, should meet multifunctional properties such as angiogenesis, osteostimulation and antibacterial properties for the treatment of large bone defects [2]. Among these properties, angiogenesis plays an important role for the formation and repair of new tissue because blood vessels provide for newly formed tissues to receive nutrients and oxygen. The stimulation of angiogenesis by the delivery of inorganic ions from biomaterial scaffolds provide to reduce cost of treatments and also prevent biological side effects when compared to the use of growth factors and so it has been attracting considerable interest in recent years [6]. The focus of this study is on advanced bioactive scaffolds enabling internal growth of tissue and controlled delivery of therapeutic ion. To be able to achieve this goal, in the first stage bioactive glass (composition in weight; 45% SiO2, 24.5% Na2O, 6% P2O5, 24.5% CaO, 2% CuO) were developed which have antibacterial and angiogenic properties. After the production of bioactive glass, bioactive glass/polymer 3D composite multifunctional scaffolds were fabricated by using foam replication technique. Then, they were coated with alginate at different percentages (in weight; 1, 2, 3 %) to improve the properties of them. The obtained scaffolds were immersed in simulated body fluid (SBF) at different time points (1, 7, 14 and 28 day) to investigate the bioactivity and biodegradability behavior of the samples. Physical and micro structural properties of the obtained scaffolds were determined by using different characterization techniques. Scanning electron microscopy investigations showed that scaffolds have highly porous structure with a good pore interconnectivity. After immersion in SBF for 28 days, the hydroxyapatite layer formation was observed significantly on the surface of the scaffolds. X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FTIR) analysis also verified the bioactivity of the obtained scaffolds. Characteristic chemical ...