GaN growth on silicon based substrates using pulsed electron beam deposition (PED) process

Abstract

Growth of GaN on Si(111) and Ge coated Si(111) using pulsed electron beam deposition (PED) process is reported. GaN was deposited on Si(111) and Ge/Si(111) at 600°C in an N2 environment without any surface pre-treatment such as pre-nitridation. X-ray diffraction confirmed that c-plane oriented GaN was grown. Photoluminescence showed near-band-edge emission, the intensity of which was improved with hydrogen passivation. Electrical characterization showed n-type conductivity with room temperature electron mobilities in the range of 300 cm2/V-sec.