Improving the efficiency of hardening of tillage machine working bodies by arc surfacing using wear-resistant rollers

Abstract

Reducing operating costs during soil processing and increasing the wear resistance of parts and components is an important condition for reducing the cost of agricultural products, increasing its efficiency and competitiveness. The development of materials with increased wear resistance and new effective technologies for strengthening working bodies in their manufacture is now becoming an urgent task. (Research purpose) The research purpose is increasing the wear resistance of the working bodies of soil-processing machines by electric arc surfacing. (Materials and methods) During the experimental study, it has been performed testing of modes and surfacing of a pilot batch of working bodies from Kverneland for field tests in VIM on an automated installation for electric arc surfacing. Authors used eutectic CastolinEnDotec DO*30 powder wire with a diameter of 1.2 millimeters and a boron content of up to 4 percent for surfacing wear-resistant rollers, which allows to obtain wear-resistant rollers with a hardness of up to 65 HRC without pores and cracks. (Results and discussion) It has been revealed that hardened ploughshares that have passed field tests are subject to lower wear rates compared to non-hardened ones. It was found that when operating time is 24.785 hectares per ploughshare, the wear of the linear size of the cutting edge along the width of hardened ploughshares is on average up to 10-11 millimeters less than that of non-hardened ones. It was found that when processing 228 hectares, the wear of the linear size of the cutting edge along the width of hardened bits is on average up to 9-10 millimeters less than that of non-hardened ones. (Conclusions) The technology of surfacing with intermittent wear-resistant rollers provides an increase in the efficiency of hardening of Kverneland working bodies according to the criterion of wear resistance by an average of 20-30 percent. The adjusted technological parameters of the surfacing process will reduce the wear rate and increase the service life of the blade part of the working bodies, as well as reduce the amount of surfaced material by an average of 60 percent. The continuation of work on strengthening the working bodies should be aimed at changing the surfacing scheme and choosing a cheaper domestic cored wire.