In Vitro Color Stability Evaluation of Three Polished and Unpolished Nanohybrid Resin Composites Immersed in a 0.12% Chlorhexidine-Based Mouthwash at Different Times

Abstract

The use of chlorhexidine-based mouthwashes on resin composites with rough surfaces can cause discoloration which compromises the esthetic of patients. The present study aimed to evaluate the in vitro color stability of Forma (Ultradent Products, Inc., South Jordan), Tetric N-Ceram (Ivoclar Vivadent, Schaan, Liechtenstein) and Filtek Z350XT (3M, ESPE, St. Paul, MN, USA) resin composites, with and without polishing, after being immersed in a 0.12% chlorhexidine (CHX)-based mouthwash at different times. The present in vitro experimental and longitudinal study used 96 nanohybrid resin composite blocks (Forma, Tetric N-Ceram and Filtek Z350XT) 8 mm in diameter and 2 mm thick, evenly distributed. Each resin composite group was divided into two subgroups (n = 16) with and without polishing and then immersed in a 0.12% CHX-based mouthwash for 7, 14, 21 and 28 days. Color measurements were performed with a calibrated digital spectrophotometer. Nonparametric tests were used to compare independent (Mann–Whitney U and Kruskal–Wallis) and related (Friedman) measures. In addition, the Bonferroni post hoc correction was used considering a significance level of p < 0.05. All polished and unpolished resin composites presented color variation < 3.3 when immersed for up to 14 days in 0.12% CHX-based mouthwash. The polished resin composite with the lowest color variation (ΔE) values over time was Forma, and the one with the highest values was Tetric N-Ceram. When comparing the color variation (ΔE) over time, it was observed that the three resin composites, with and without polishing, presented a significant change (p < 0.001), although these changes in color variation (ΔE) were evident from 14 days between each color acquisition (p < 0.05). The unpolished Forma and Filtek Z350XT resin composites showed significantly more color variation than the same polished ones at all times when immersed in a 0.12% CHX-based mouthwash for 30 s daily. In addition, every 14 days, all three resin composites with and without polishing showed a significant color change, while, every 7 days, color stability was maintained. All the resin composites showed clinically acceptable color stability when exposed for up to 14 days to the above-mentioned mouthwash.

Properties of Nanohybrid Dental Composites—A Comparative In Vitro Study

“…The composition of the resin materials and the relative amount of resin and filler content represent key factors in long-term color stability. Low-filler-content-resin-based materials have a reduced color stability due to increased water sorption [37]. Small particle fillers in composite resins determine a high color stability, compared to composites with large filler particles; this explains our result showing that HU is more stain-resistant than is CM.…”