Low temperature molten salt synthesis of porous La1-Sr Mn0.8Fe0.2O3 (0 ≤ x ≤ 0.6) microspheres with high catalytic activity for CO oxidation

Huang, Xuehui; Niu, Pengju; Shang, Xiaohui

doi:10.1016/s1872-2067(16)62502-0

Cited by 4 publications

(1 citation statement)

References 32 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…To increase the surface area of perovskite-type catalysts, many investigators have developed new methods. For example, our group prepared porous La 1−x Sr x Mn 0.8 Fe 0.2 O 3 (0≤x≤0.6) microspheres with a surface area of 55.73 m 2 •g −1 through a low temperature molten salt approach 9 . Furthermore, some researchers dispersed perovskite catalysts on high surface area supports, e.g., mesoporous SiO 2 10 , SBA-15, MCM-41 11 ,…”

Section: Introductionmentioning

confidence: 99%

Surface Modification of SBA-15 and Its Effect on the Structure and Properties of Mesoporous La0.8Sr0.2CoO3

Huang¹,

Shang²,

Niu³

2017

Acta Physico-Chimica Sinica

View full text Add to dashboard Cite

摘要：本文通过改进的水热法制备了孔径较大的有序介孔 SBA-15，其孔径(Dp)为 10.1 nm，并采用浓盐酸、三甲基氯硅烷(TMCS)和 3-氨丙基三乙氧基硅烷(APTES)对 SBA-15 表面进行了羟基、甲基和氨基改性处理。以嫁接不同表面官能团的 SBA-15 为模板，合成了一系列菱方晶系钙钛矿型介孔 La0.8Sr0.2CoO3 氧化物，系统地研究了模板 SBA-15 的表面性能对 La0.8Sr0.2CoO3 氧化物结构和性能的影响。X 射线衍射(XRD)图谱表明，外表面引入-CH3，内表面羟基化和引入-NH2 的模板有利于合成结晶度较高的、物相单一的钙钛矿结构氧化物。小角 XRD 图谱、高分辨率透射电子显微镜(HRTEM)图像以及 N2 吸附测试结果表明，所制备的催化剂为介孔结构。CO 氧化的催化活性测试表明，采用表面改性的模板合成的 La0.8Sr0.2CoO3 氧化物表现出较高的催化活性和稳定性，在 140 °C 时可以实现 CO 的完全转化，连续使用 100 h 后催化剂的催化活性几乎没有下降。X 射线光电子能谱(XPS)、H2 程序升温还原(H2-TPR)和 O2 程序升温脱附(O2-TPD)测试结果表明，催化剂表面丰富的吸附氧物种，高价态的 Co 离子，钙钛矿结构中 Sr 在表面富集，及优良的低温氧化还原性是催化活性提高的主要原因。关键词：SBA-15；表面改性；模板法；介孔 La0.8Sr0.2CoO3；低温 CO 氧化中图分类号：O643；TQ138.1+2