Optimasi Parameter Proses 3D Printing Terhadap Kuat Tarik Material Filamen PLA + Menggunakan Metode Taguchi

Abstract

FDM (Fused Deposition Modeling) is one of the methods often usen by researchers in 3D printing technology which is used to print filaments products as a materials, due to the easy technique for 3D printing with relatively low production costs. One of the materials that can be processed in a 3D printing machine ia PLA+. Research in tensile testing has been done on PLA and ABS filaments. Meanwhile, tensile testing using PLA+ filaments is still rarely done. From these problems, research is needed to get the optimal process parameters on the 3D printing machine to get the highest tensile strenght value using PLA+ filaments. This research uses the taguchi method, carried out on a PRUSA area model FDM 3D Printing machine with dimensions of 300mm x 300mm x 350mm using a nozzle size of 0.4mm. The material used is PLA + Esun filament with a diameter of 1.75 mm with a variety of printing speed parameters (30 mm/s, 35 mm/s, 40 mm/s, 45 mm/s, 50 mm/s), nozzle temperature (1950C, 2000C, 2050C, 2100C, 2150C), layer thickness (0.10mm, 0.15mm, 0.20mm, 0.25mm, 0.30mm), cooling speed (20%, 40%, 60%, 80%, 100%), orientation (00, 300, 450, 600,900) which will be determined in ideamaker 3.6.1 to produce 75 printed samples. This research aims to determine the optimal tensile strength value. From the research results there is an optimal tensile strength value, namely in experiment 10 with the parameter values of printing speed (35 mm/s), Nozzle Tenperature (2150C), Layer Thickness (0.10mm), Cooling speed (20%), and Orientation (450). with a tensile strength value of 48.1 MPa from 3 replications.

Optimasi Multi Parameter Mesin 3d Printer FDM Untuk Material Thermoplastic Polyurethane Guna Menghasilkan Error Dimensi Terkecil Menggunakan Metode 2k Factorial Design

“…Penggunaan dalam industri manufaktur, 3D Printing digunakan sebagai sarana untuk membuat purwarupa (prototype). Pada pembuatan benda kerja, Teknologi 3D Printing membuat benda padat tiga dimensi dari suatu desain digital [3]. Terdapat beberapa macam Teknologi 3D Printing, seperti Fused Depositon Modeling (FDM), Stereolithography Apparatus (SLA), Selective Laser Sintering (SLS), dan Digital Light Processing (DLP).…”

“…FDM merupakan salah satu teknologi 3D printing yang banyak digunakan. Hal tersebut dikarenakan pengoperasiannya yang relatif sederhana, biaya yang relatif murah, serta berbagai jenis material yang dapat diakses di pasar [3]. Proses kerja FDM Optimasi Multi Parameter Mesin 3D Printer FDM untuk Material Thermoplastic Polyurethane Guna Menghasilkan Error Dimensi Terkecil Menggunakan Metode 2 K Factorial Design Hudan Ahmad Latif, Ibnu Abdul Rosid, Grita Supriyanto Dewi, Maria Gratiana Dian Jatiningsih menggunakan material polimer berbentuk filamen, kemudian filamen dipanaskan dan diekstrusi melalui nozzle pada meja printer secara lapis demi lapis hingga terbentuk objek tiga dimensi sesuai dengan desain objek tiga dimensi [4].…”

Analisis dan Optimasi 3D Print Material Carbon Fiber Pla Menggunakan Metode Taguchi-Gra

“…3D printing yang umum digunakan adalah metode FDM (Fused Deposition Modelling). Prinsip kerja dari FDM ini adalah dengan mengesktruksi filamen thermoplastic melalui nozzle yang dipanaskan dan dicetak lapis demi lapis [3].…”

Optimasi Parameter Produk 3D Printing Terhadap Kekuatan Bending Dengan Menggunakan Filamen Nylon

“…Metode FDM cenderung memiliki sifat mekanik yang lebih rendah dikarenakan kekuatan ikatan antar lapisan lebih kecil dan produk hasil metode FDM seringkali menyusut mengakibatkan dileminasi diantara lapisannya. Selain itu, ada inner stress yang dapat mengakibatkan objek FDM menjadi retak kerena mengalami pendinginan yang cepat dari titik leleh ke suhu ruangan [5]. Nylon (poliamida) merupakan bahan yang populer di industri plastik karena memiliki ketangguhan dan fleksibilitas yang baik.…”