Phase Transformation Behavior of Polylactide Probed by Small Angle Light Scattering and Calorimetry

Abstract

Small angle light scattering (SALS) and differential scanning calorimetry DSC have been applied to investigate the melting of spherulites isothermally crystallized polylactide. At an isothermal crystallization temperature high enough, pure α-phase crystals are formed. Exposed to a temperature gradient, the crystals first melt and then recrystallize before they finally melt. With decreasing crystallization temperature, an increasing fraction of polylactide is crystallizing in the less stable α 0 -phase.α 0 -crystals also melt upon increasing the temperature but recrystallize to the more stable α-phase. A constant spherulite size is revealed by SALS for both processes, the α/α and α 0 /α meltrecrystallization, until completion of the final melting, thereby supporting integrity of the spherulites throughout the entire processes. Joint DSC and SALS experiments demonstrate that the depolarized scattering invariant correlates with the heat flow recorded by DSC and thus offer an alternative measure for the degree of crystallinity. The following mechanism is identified for both processes: initial melting and recrystallization overlay each other. Crystallinity is not fully recovered upon recrystallization because only part of the original lamellae survives the melt-recrystallization, though with an increased thickness. While lamellae are melting and reforming or simply transforming their phase, the spherulites survive the process until final melting.

Properties of Stereocomplex PLA for Melt Spinning

“…M W and PDI refer to molecular weight and polydispersity index, respectively. M W and PDI of PDLA [26] and PLLA [27] were taken from the literature, M W and PDI of msPLA were provided by NatureWorks.…”

Assessment of Polylactide as Optical Material

“…As PLA shows excellent optical properties in its glassy state, as well as high resistance to radiation induced aging, its use for optical applications seems consequential 38,91 . However, close to its Tg PLA crystallizes and turns hazy 78,79 . As many applications require optical materials to be heated to 50°C and above 78 , the crystallization of PLA has to be adapted to favor its application in optics.…”