Relationship between test severity and wear mode transition in micro-abrasive wear tests

Cozza, Ronaldo Câmara; Mello, José Daniel Biasoli de; Tanaka, Deniol Katsuki; Souza, R.M.

doi:10.1016/j.wear.2007.01.099

Cited by 63 publications

(52 citation statements)

References 29 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…In microabrasive wear, the wear mode can occur by scratching, rolling or a combination of both 19 . The wear rolling occurs when abrasives roll over the wear surface, while the wear scratching occurs when the abrasives sliding over the wear surface 19,20 .…”

Section: Resultsmentioning

confidence: 99%

Micro Abrasive Wear Behaviour Study of Carburization and Ion Plasma Nitriding of P20 Steel

et al. 2016

View full text Add to dashboard Cite

P20 steel, which is mainly used in plastic molds, was thermochemically treated by ion plasma nitriding and solid and gas carburization. In this work, the solid and gas carburization were performed at 925 ºC for four different durations. The ion plasma nitriding was performed at 520 ºC for four different durations. The thermochemical treatment increased the micro abrasive wear resistance of the studied material. The gas carburizing treatment resulted in a greater surface microhardness. Longer treatment times increased the effectiveness of the thickness layer in all cases. The solid carburization produced a larger thickness layer than the gas carburization and ion nitriding.

show abstract

Section: Resultsmentioning

confidence: 99%

Micro Abrasive Wear Behaviour Study of Carburization and Ion Plasma Nitriding of P20 Steel

et al. 2016

View full text Add to dashboard Cite

show abstract

“…Testes de micro-abrasão usam um fluido para transportar as partículas abrasivas para a superfície de contato ativa e a água destilada é normalmente usada para este propósito [28][29][30][31][32][33][34][35][36][37][38][39][40]. É muito bem conhecido que os aços inoxidáveis podem formar uma camada passiva autoregenerativa em diferentes meios, de acordo com Massoud et al [41], a água é um meio passivante para os aços inoxidáveis.…”

Section: Testesunclassified

Abrasão-Corrosão: Novas Informações a Partir Da Medida Das Forças No Contato

Santos¹,

Labiapari²,

Ardila³

et al. 2018

ABM Proceedings

View full text Add to dashboard Cite

ResumoVisando o estudo da sinergia entre abrasão e corrosão concebeu-se um novo instrumento, permitindo a medição das forças que atuam sobre o contacto. O dispositivo consiste de um equipamento de micro-abrasão por esfera fixa dotada de uma célula de carga de três eixos, e uma célula eletroquímica. Uma membrana protetora flexível foi desenvolvida para isolar a célula de carga, situado no exterior da célula eletroquímica, da amostra no interior da célula. Uma solução corrosiva com partículas abrasivas é continuamente alimentada no contacto entre a amostra e a esfera. Os ensaios de abrasão-corrosão foram realizados simultaneamente em aços inoxidáveis e ferríticos. Também foram executados ensaios de micro-abrasão e corrosão separadamente para avaliar a capacidade do equipamento nos estudos da sinergia entre a micro-abrasão e a corrosão. Para as três condições de ensaios (micro-abrasão, corrosão e abrasão-corrosão) o equipamento se mostrou eficiente em evidenciar a variação nas propriedades do material com excelente repetibilidade. Para os aços austeníticos, as mudanças nas condições de carregamento nos ensaios de abrasão-corrosão induziram variações significativas nas curvas de polarização. A capacidade única de acompanhar as forças que atuam sobre o contato dos processos de abrasão-corrosão pode abrir caminho para novas descobertas sobre o estudo da sinergia na abrasão-corrosão, em especial, a dissipação de energia na interface quantificada através do coeficiente de atrito. Palavras-chave: Abrasão-Corrosão; Aço inoxidável; Equipamento; Medida de força. ABRASION-CORROSION: NEW INSIGHTS FROM FORCE MEASUREMENTS AbstractAiming at the study of synergy between the abrasion and corrosion a new instrument, enabling the measurement of forces acting on the contact, has been designed. The test rig consists of a fixed-ball micro-abrasion tester, where the specimen is supported by a threeaxis load cell, and an electrochemical cell. A very flexible protective membrane has been designed to isolate the load cell, located outside the electrochemical cell, from the sample inside the cell. A mixture of a corrosive fluid and abrasive particles is continuously fed to the contact. Simultaneous micro-abrasion/corrosion tests have been performed in austenitic and ferritic stainless steels. In addition, independent micro-abrasion and corrosion tests were also carried out to evaluate the capacity of the rig to account for the synergy between microabrasion and corrosion. For all three tests (micro-abrasion, corrosion and combined microabrasion/corrosion) the rig was efficient to respond to variation in material properties and showed excellent repeatability. For the austenitic steels, changes in loading conditions in combined micro-abrasion and corrosion tests induced significant variations on polarization curves. The unique capability of monitoring the forces acting on the contact of abrasioncorrosion processes could pave the way for new insights into the study of abrasioncorrosion, in particular the dissipation of energy at the interface q...

show abstract

“…A abrasão a 3-corpos, denominada abrasão por rolamento, acontece quando as partículas abrasivas não ficam presas à superfície da esfera, mas rolam na região de contato (rolling wear) produzindo uma superfície altamente deformada por múltiplas micro-penetrações, sem direção preferencial evidente, sendo dominante em condições de baixas forças aplicadas e altas concentrações de partículas abrasivas. Já a abrasão a 2-corpos, denominada abrasão por deslizamento ou riscamento, acontece quando a partí-cula abrasiva se prende à esfera e atuam como micro-corte e sulcam ou arrancam micro-cavacos da região de contato (grooving wear), produzindo uma série de riscos paralelos na superfície, sendo dominante para condições de altas forças aplicadas e/ou suspensão abrasiva de baixa concentração [27,28,29,30]. De acordo com BOZE et al [27] para utilizar o teste de microabrasão para avaliar a resistência ao desgaste de um sistema seria essencial assegurar a ocorrência de um único mecanismo de abrasão, no entanto os dois mecanismos podem ocorrer simultaneamente, produzindo o modo de desgaste misto.…”

Section: Ensaio De Desgaste No Aço Aisi 420 Temperado E Revenidounclassified

Desenvolvimento de dispositivo e estudo do comportamento ao microdesgaste abrasivo do aço AISI 420 temperado e revenido

et al. 2015

View full text Add to dashboard Cite

O objetivo deste trabalho é a construção de um dispositivo para a realização de ensaios de micro desgaste abrasivo por esfera fixa. O contato abrasivo é realizado por uma esfera de aço AISI 52100, a qual é presa num eixo que gira com grande precisão, com ajuda de um motor, em relação a uma amostra plana que se manterá estacionária. A carga normal de ensaio é aplicada através de ajustes de peso no suporte pivotado do corpo de prova, a qual pode ser variada a cada ensaio realizado. Este dispositivo foi utilizado para a determinação da resistência ao desgaste abrasivo e da eficácia de tratamentos de superfície utilizados em peças que sofrem este tipo de solicitação em serviço, além de utilizá-lo para estudar novos produtos desenvolvidos para o aumento de resistência ao desgaste de superfícies. Foi avaliada a resistência ao microdesgaste abrasivo de aço AISI 420 temperado e revenido. Observou-se que o aumento da dureza do material tratado aumentou a resistência ao desgaste abrasivo quando comparado com o material sem tratamento térmico.Palavras-chave: desgaste microabrasivo, esfera fixa, aço AISI 420, configuração experimental. ABSTRACTThe abrasive microwear testing has been the subject of a significant amount of research in recent years, when its potential to evaluate the behaviour of thin coating became relevant. The aim of this work is to build a apparatus for abrasive microwear testing by rotating sphere. The abrasive contact is performed by a AISI 52100 steel ball which rotates, with great accuracy with the help of an electric motor, in relation to a flat sample that will remain stationary. The normal load is applied by weight adjustments in the support of the test specimen, which can be varied for each performed test. This device was used to determine the abrasive wear resistance and effectiveness of surface treatments used in parts that undergo this kind of requirement in service, and also for studying new products developed for increasing the wear resistance of surfaces. The microwear resistance of the quenched and tempered AISI 420 steel was evaluated. It was observed that increasing the hardness of the treated material produced an increased wear resistance when compared with untreated material Keywords: microabrasive wear, rotating sphere, stainless steel AISI 420, experimental setup. INTRODUÇÃOA palavra tribologia, derivada do grego, significa estudo do atrito, sendo a ciência e tecnologia que estuda a Matéria, v.20, n.2, pp. 304 -315, 2015.

show abstract

Relationship between test severity and wear mode transition in micro-abrasive wear tests

Cited by 63 publications

References 29 publications

Micro Abrasive Wear Behaviour Study of Carburization and Ion Plasma Nitriding of P20 Steel

Micro Abrasive Wear Behaviour Study of Carburization and Ion Plasma Nitriding of P20 Steel

Abrasão-Corrosão: Novas Informações a Partir Da Medida Das Forças No Contato

Desenvolvimento de dispositivo e estudo do comportamento ao microdesgaste abrasivo do aço AISI 420 temperado e revenido