Residual Stresses on Various PVD Hard Coatings on Tube and Plate Substrates

Abstract

In this study, the average residual stresses were determined in hard PVD nACRo (nc-AlCrN/a-Si3N4), nACo (nc-AlTiN/a-Si3N4), AlCrN, TiAlN, and TiCN commercial coatings through the deflection of the plate substrates and the simultaneous measurement of length variation in thin-walled tubular substrates. The length measuring unit was used for the measurement of any length change in the tubular substrate. A change in tube length was reduced to the deflection of the middle cross-section of the elastic element for which deformation was measured using four strain gauges. The cross-sectional microstructure and thickness of the coatings were investigated by means of scanning electron microscopy (SEM), and a determination was made of the chemical composition of the coatings and substrate by means of energy dispersive X-ray spectroscopy (EDS). The values of average compressive residual stresses, as determined by both methods, were very high (with a variation of between 2.05 and 6.63 GPa), irrespective of coating thickness, but were dependent upon the shape of the substrate and on its position in relation to the axis of the rotating cathode. The thicknesses of the coatings that were deposited on the plates with two parallel fixings (such as the nACRo coatings on the front surface at 6.8 μm and on the rear surface at 2.9 μm) and on the tubular substrates (10.0 μm) were significantly different. The higher average compressive residual stresses in the coating correlate to the higher average relative wear resistance that was obtained during field wear testing.