Study of Temperature Sintering by Microwave Energy in Ferrites Ni_0,5Zn_0,5Fe₂O₄

Abstract

This study proposes to evaluate the influence of the variation of sintering temperature on microstructural characteristics and magnetic ferrite Ni0,5Zn0,5Fe2O4sintered by microwave energy. The samples were sintered at 900, 1000, 1100 and 1200°C for exposure time of 10 minutes, with rate 50°C/minutes and characterized by density and porosity, X-ray diffraction, scanning electron microscopy and magnetic measurements. The results indicate that the values of density and apparent porosity were 4.2, 4.5, 4.4 and 4.5 g/cm3and 3.4, 2.1, 2.2 and 2.4% for the sintering temperatures of 900, 1000, 1100 and 1200°C respectively. The formation of the ferrite phase Ni0,5Zn0,5Fe2O4been identified for all conditions of sintering, with grain sizes of 52, 62, 71 and 58nm and saturation magnetization values of 63, 68, 69 and 27 emu/g to temperatures sintering 900, 1000, 1100 and 1200°C respectively.