Surface layer structure of AISI 1020 steel at different stages of dry sliding under electric current of high density

Abstract

Abstract. Wear intensity of the sliding electric contact steel 1020/steel 1045 depending on sliding time is presented at the contact current density higher than 100 A/cm 2 without lubricant. It is shown that wear intensity of 1020 steel decreases at increasing of sliding time. Wear intensity is stabilized after some sliding time. This time (burn-in time) decreases at reduction of current density. Structural changes are realized in surface layer. Signs of liquid phase are observed on sliding surface. This liquid isn't a result of melting. It is established using Auger spectrometry that the contact layer contains up to 50 at.% of oxygen.