The Study on the Corrosion Property of the Zn-Mg Alloy Coatings with Various Mg Contents using EIS Measurement

Abstract

In this study, the Zn-Mg alloy coatings with various Mg contents were deposited using an unbalanced magnetron sputtering process. Their surface microstructure, chemical composition, phase, and corrosion property were investigated. The microstructure of the Zn-Mg coatings changed from porous microstructure to dense one with increasing Mg contents in the coatings. As Mg contents in coatings increased, intermetallic phases such as Mg 2 Zn 11 and MgZn 2 were detected from X-ray diffraction (XRD) results. The corrosion resistance of the Zn-Mg alloy coatings was investigated quantitatively using electrochemical impedance spectroscopy (EIS) measurement with 3.5% NaCl solution. The results of EIS measurement showed that the charge transfer resistance and the phase angle of the Zn-Mg alloy coatings were increased from 162.1 Ω·cm 2 to 558.8 Ω·cm