Thermoplastic polyurethane–urea elastomers with superior mechanical and thermal properties prepared from alicyclic diisocyanate and diamine

Abstract

High‐performance thermoplastic polyurethane (TPU) elastomers have long been the objective of numerous studies. In this work, thermoplastic polyurethane–urea (TPUU) elastomers with balanced superior mechanical and thermal properties, in comparison with the rare cases of high‐performance TPU/TPUU elastomers with super‐high tensile strength, were synthesized by the reaction of polycarbonate diols with excess alicyclic isophorone diisocyanate, followed by the chain extension of alicyclic isophorone diamine. When the content of hard segment was around 47%, the TPUU elastomer had super‐high tensile strength of 51.7 MPa, initial elastic modulus of 698 MPa and elongation at break of 480%. The temperature range of this TPUU elastomer's rubbery state was up to 120°C with storage modulus above 200 MPa, and its rubbery flow state reached 200°C where the storage modulus was still as high as 100 MPa. Fourier transform infrared spectroscopy analysis indicated the presence of strongly hydrogen bonded urethane and urea groups in these TPUU elastomers. Atomic force microscopy and differential scanning calorimetry studies demonstrated significant and nearly perfect microphase separation in these TPUU elastomers when the hard segment content was around or below 47%. These noncrystalline TPUU elastomers could be thermally processed or processed in the form of a solution.

Study and Characterization of Regenerated Hard Foam Prepared by Polyol Hydrolysis of Waste Polyurethane

“…PU can be used to prepare soft polyurethane foam, hard polyurethane foam, polyurethane elastomers, coatings, adhesives, and other products [ 6 ] which are deeply loved by people. Thermoplastic polyurethane elastomers, with their excellent properties and wide application, have become important thermoplastic elastomer materials whose molecules are largely linear, with no or little chemical cross-linking [ 7 , 8 ]. There are many physical cross-links formed by hydrogen bonds between linear polyurethane molecular chains, which strengthen the material’s form and endow it with many excellent properties, such as a high modulus, high strength, and excellent wear resistance, chemical resistance, hydrolysis resistance, high and low temperature resistance, and mold resistance [ 9 , 10 , 11 , 12 , 13 , 14 ].…”

Healable and reprocessable silica/poly(oxime‐urethane) composite elastomer with high mechanical robustness and exceptional damage‐tolerant capacity

“…The rapid development of elastomers holds great promise for a wide range of applications in industry, medical devices and aerospace exploration to soft robotics and wearable electronics. [1][2][3][4][5][6][7] Due to the high entropy-elasticity, elastomers can dissipate mechanical energy and recover their original shape and mechanical properties after multiple deformations. 8 Conventional elastomers usually suffer from crack sensitivity and low fracture strength.…”

Preparation and Characterization of Tilapia Collagen-Thermoplastic Polyurethane Composite Nanofiber Membranes

“…Thermoplastic polyurethane (TPU) is an elastomeric polymer with excellent mechanical properties, wear resistance, good elasticity, and toughness [ 17 ]. TPU also has good degradability when hydrolyzed, oxidized, or enzymatically degraded in vivo [ 18 ].…”