Two-Dimensional Nanosheets Produced by Liquid Exfoliation of Layered Materials

Abstract

One sentence summary:We describe a general liquid-phase method to exfoliate layered compounds to give monoand few-layer flakes in large quantities. TMDs consist of hexagonal layers of metal atoms, M, sandwiched between two layers of chalcogen atoms, X, with stoichiometry MX 2 . While the bonding within these tri-layer sheets is covalent, adjacent sheets stack via van der Waals interactions to form a 3D crystal. TMDs occur in more than 40 different types (2, 3) depending on the combination of chalcogen (S, Se or Te) and transition metal(3). Depending on the co-ordination and oxidation state of the metal atoms, TMDs can be metallic, semi-metallic or semiconducting(2, 3), e.g. WS 2 is a semiconductor while NbSe 2 is a metal(3). In addition, superconductivity(4) and charge density wave effects(5) have been observed in some TMDs. This versatility makes them potentially useful in many areas of electronics.However, like graphene(6), layered materials must be exfoliated to fulfil their full potential. For example, films of exfoliated Bi 2 Te 3 should display enhanced thermoelectric efficiency by suppression of thermal conductivity(7). Exfoliation of 2D topological insulators such as Bi 2 Te 3 and Bi 2 Se 3 would reduce residual bulk conductance, 4 highlighting surface effects. In addition, we can expect changes in electronic properties as the number of layers is reduced e.g. the indirect bandgap of bulk MoS 2 becomes direct in few-layer flakes(8). Although exfoliation can be achieved mechanically on a small scale(9, 10), liquid phase exfoliation methods are required for many applications(11).Critically, a simple liquid exfoliation method would allow the formation of novel hybrid and composite materials. While TMDs can be chemically exfoliated in liquids(12-14), this method is time consuming, extremely sensitive to the environment and incompatible with most solvents.We demonstrate exfoliation of bulk TMD crystals in common solvents to give mono-and few layer nano-sheets. This method is insensitive to air and water and can potentially be scaled up to give large quantities of exfoliated material. In addition, we show that this procedure allows the formation of hybrid films with enhanced properties.We initially sonicated commercial MoS 2 , WS 2 and BN (15, 16) powders in a number of solvents with varying surface tensions. The resultant dispersions were centrifuged and the supernatant decanted (Section S3). Optical absorption spectroscopy showed that the amount of material retained (characterised by / A l C α = , where A/l is the absorbance per length, α is the extinction coefficient and C is the concentration) was maximised for solvents with surface tension close to 40 mJ/m 2 (17, 18) ( Fig. 1A-C). Detailed analysis, within the framework of Hansen solubility parameter theory(19), shows successful solvents to be those with dispersive, polar and H-bonding components of the cohesive energy density within certain well-defined ranges (Section S4, Figs. S2-S3). This can be interpreted to mean that successful solvents are those w...

Emerging Trends in Phosphorene Fabrication towards Next Generation Devices

“…The NMP solvent for obtaining stable, highly concentrated (≈0.4 mg mL –1 ) BP dispersions was used in LPE in most of the reported studies 12, 67, 85, 91, 95, 118, 160, 166, 183, 185, 186, 187. NMP and DMF are well suit for liquid exfoliation owing to their relatively high boiling points and surface tension (≈40 mJ m –2 ) 166, 183, 188.…”

“…NMP and DMF are well suit for liquid exfoliation owing to their relatively high boiling points and surface tension (≈40 mJ m –2 ) 166, 183, 188. However, phosphorene, extracted by NMP solution, cannot be used directly either in the fabrication of electronic devices or for optical investigations because of its poor volatility.…”

Periodic Organic–Inorganic Halide Perovskite Microplatelet Arrays on Silicon Substrates for Room‐Temperature Lasing

“…The atomically thin crystalline, single layer h‐BN materials29, 30, 31 function as the intermediate layer and growth nuclei that provide not only an epitaxial intermediary between the substrate and the perovskite, but also as a cladding layer for better optical confinement in lasing due to its large bandgap. Furthermore, the h‐BN can also serve as a superior insulating dielectric layer (as compared to other layered materials like graphene, MoS 2 and black phosphor) for preventing shorts in practical devices 28, 32, 33.…”

Fabrication of flexible and freestanding zinc chalcogenide single layers

“…Although the IGAs often bring on a wealth of innovative applications, their species are still only limited to layered compounds. In other words, controllable exfoliation of layered compounds is regarded as the exclusive way to obtain single-layered IGAs with few atomic thickness [7][8][9] , whereas the hard bond-cleavage of non-layered compounds enables the fabrication of their single layers with few atomic thickness become a great challenge. Despite recent progress in fabricating CdSe 2D sheets with few atomic thickness 10,11 , the difficulties in the removal of nonvolatile organic solvents and the occurrence of aggregation during slow solvent evaporation unfortunately bring difficulty to process them into devices 12 .…”