Vulcan carbon was pre-treated at 850 o C at a ramp rate of 5 o C/min and maintained for 24 hours under 5% H2 in Ar. Cs-Ru modified MgO and AC preparationTypically, Ru3(CO)12 was dispersed in THF for 2 hours under sonication. The mixture was then transferred to the MgO or activated carbon (AC) and allowed to sonicate at ambient

The ambient-pressure endstation and branchline of the Versatile Soft X-ray (VerSoX) beamline B07 at Diamond Light Source serves a very diverse user community studying heterogeneous catalysts, pharmaceuticals and biomaterials under realistic conditions, liquids and ices, and novel electronic, photonic and battery materials. The instrument facilitates studies of the near-surface chemical composition, electronic and geometric structure of a variety of samples using X-ray photoelectron spectroscopy (XPS) and near-edge X-ray absorption fine-structure (NEXAFS) spectroscopy in the photon energy range from 170 eV to 2800 eV. The beamline provides a resolving power hν/Δ(hν) > 5000 at a photon flux > 1010 photons s−1 over most of its energy range. By operating the optical elements in a low-pressure oxygen atmosphere, carbon contamination can be almost completely eliminated, which makes the beamline particularly suitable for carbon K-edge NEXAFS. The endstation can be operated at pressures up to 100 mbar, whereby XPS can be routinely performed up to 30 mbar. A selection of typical data demonstrates the capability of the instrument to analyse details of the surface composition of solid samples under ambient-pressure conditions using XPS and NEXAFS. In addition, it offers a convenient way of analysing the gas phase through X-ray absorption spectroscopy. Short XPS spectra can be measured at a time scale of tens of seconds. The shortest data acquisition times for NEXAFS are around 0.5 s per data point.

Hydrogen spillover is the phenomenon where a hydrogen atom, generated from the dissociative chemisorption of dihydrogen on the surface of a metal species, migrates from the metal to the catalytic support. This phenomenon is regarded as a promising avenue for hydrogen storage, yet the atomic mechanism for how the hydrogen atom can be transferred to the support has remained controversial for decades. As a result, the development of catalytic support for such a purpose is only limited to typical reducible oxide materials. Herein, by using a combination of in situ spectroscopic and imaging technique, we are able to visualize and observe the atomic pathway for which hydrogen travels via a frustrated Lewis pair that has been constructed on a nonreducible metal oxide. The interchangeable status between the hydrogen, proton, and hydride is carefully characterized and demonstrated. It is envisaged that this study has opened up new design criteria for hydrogen storage material.

In situ surface sensitive XPS and NEXAFS clarify the promotion effect of Fe in Ni–Fe/hydrotalcite-derived catalysts for the CO2 methanation reaction.