In the search for novel solid electrolytes for solid-state batteries, thiophosphate ionic conductors have been in recent focus owing to their high ionic conductivities, which are believed to stem from a softer, more polarizable anion framework. Inspired by the oft-cited connection between a soft anion lattice and ionic transport, this work aims to provide evidence on how changing the polarizability of the anion sublattice in one structure affects ionic transport. Here, we systematically alter the anion framework polarizability of the superionic argyrodites LiPSX by controlling the fractional occupancy of the halide anions (X = Cl, Br, I). Ultrasonic speed of sound measurements are used to quantify the variation in the lattice stiffness and Debye frequencies. In combination with electrochemical impedance spectroscopy and neutron diffraction, these results show that the lattice softness has a striking influence on the ionic transport: the softer bonds lower the activation barrier and simultaneously decrease the prefactor of the moving ion. Due to the contradicting influence of these parameters on ionic conductivity, we find that it is necessary to tailor the lattice stiffness of materials in order to obtain an optimum ionic conductivity.

The solid lithium-ion electrolyte ''Li 7 La 3 Zr 2 O 12 '' (LLZO) with a garnet-type structure has been prepared in the cubic and tetragonal modification following conventional ceramic syntheses routes. Without aluminium doping tetragonal LLZO was obtained, which shows a two orders of magnitude lower room temperature conductivity than the cubic modification. Small concentrations of Al in the order of 1 wt% were sufficient to stabilize the cubic phase, which is known as a fast lithium-ion conductor. The structure and ion dynamics of Al-doped cubic LLZO were studied by impedance spectroscopy, dc conductivity measurements, 6 Li and 7 Li NMR, XRD, neutron powder diffraction, and TEM precession electron diffraction. From the results we conclude that aluminium is incorporated in the garnet lattice on the tetrahedral 24d Li site, thus stabilizing the cubic LLZO modification. Simulations based on diffraction data show that even at the low temperature of 4 K the Li ions are blurred over various crystallographic sites. This strong Li ion disorder in cubic Al-stabilized LLZO contributes to the high conductivity observed. The Li jump rates and the activation energy probed by NMR are in very good agreement with the transport parameters obtained from electrical conductivity measurements. The activation energy E a characterizing longrange ion transport in the Al-stabilized cubic LLZO amounts to 0.34 eV. Total electric conductivities determined by ac impedance and a four point dc technique also agree very well and range from 1 Â 10 À4 Scm À1 to 4 Â 10 À4 Scm À1 depending on the Al content of the samples. The room temperature conductivity of Al-free tetragonal LLZO is about two orders of magnitude lower (2 Â 10 À6 Scm À1 , E a = 0.49 eV activation energy). The electronic partial conductivity of cubic LLZO was measured using the Hebb-Wagner polarization technique. The electronic transference number t eÀ is of the order of 10 À7. Thus, cubic LLZO is an almost exclusive lithium ion conductor at ambient temperature.

Solid-state batteries with inorganic solid electrolytes are currently being discussed as a more reliable and safer future alternative to the current lithium-ion battery technology. To compete with state-of-theart lithium-ion batteries, solid electrolytes with higher ionic conductivities are needed, especially if thick electrode configurations are to be used. In the search for optimized ionic conductors, the lithium argyrodites have attracted a lot of interest. Here, we systematically explore the influence of aliovalent substitution in Li 6+x P 1−x Ge x S 5 I using a combination of X-ray and neutron diffraction, as well as impedance spectroscopy and nuclear magnetic resonance. With increasing Ge content, an anion site disorder is induced and the activation barrier for ionic motion drops significantly, leading to the fastest lithium argyrodite so far with 5.4 ± 0.8 mS cm −1 in a cold-pressed state and 18.4 ± 2.7 mS cm −1 upon sintering. These high ionic conductivities allow for successful implementation within a thick-electrode solid-state battery that shows negligible capacity fade over 150 cycles. The observed changes in the activation barrier and changing site disorder provide an additional approach toward designing better performing solid electrolytes.