The accumulation of petroleum products causes damage to ecosystems, which can be avoided with cellulose-based products. The influence of different ratios of cellulose micro/nanofibrils (MFC/NFC) on the properties of hydroxypropyl methylcellulose (HPMC) films was evaluated. Films were prepared using proportions of 0, 25, 50, 75 and 100 % (w/w) of MFC/NFC from Pinus sp. in relation to HPMC. Physical, barrier, surface, optical, morphological and mechanical properties were evaluated. Solids content, basis weight and density values increased with higher amount of MFC/NFC and thickness and porosity were reduced. SEM images showed that films with more than 50 % MFC/NFC had a more granular surface, which decreased transparency from 80 to 65 %. Water vapor penetration did not differ between films and degradation in water was reduced from 40 to 5 % with MFC/NFC addition. There were no differences in contact angle and wettability, but all films showed high resistance to fat penetration. Films with MFC/NFC content between 75 and 100 % showed higher values for tensile strength (50 to 65 MPa) and Young’s modulus (6 to 10 MPa) and lower elongation at break (1 to 2 %). The experimental results indicated that films with MFC/NFC content above 50 % have potential to be used as packaging material.

A demanda por produtos a base de madeira é crescente, principalmente a partir de florestas plantadas.  Dessa forma é possível maximizar o aproveitamento da madeira e obter produtos com resistência e confiabilidade de utilização. Objetivou-se estudar as propriedades tecnológicas d compensado e do LVL (Laminated Veneer Lumber) produzidos com madeira de paricá (Schizolobium amazonicum Huber ex Ducke). Avaliou-se a absorção de água, densidade (básica e aparente), umidade, porosidade, inchamento em espessura e inchamento residual. Utilizou-se 30 corpos de prova de cada tipo de painel, os dados foram analisados por meio de estatística descritiva e pela matriz de correlação de Pearson. No compensado a densidade básica, densidade aparente e porosidade foram de 0,38 g cm-3, 0,44 g cm-3 e 75,47%, respetivamente. Ainda, a umidade elevou-se 20,91% entre 2 e 96 horas de imersão em água. O inchamento residual foi de 3,75% e o inchamento em espessura aumentou 0,81% entre 2 e 96 horas de imersão. No LVL, a densidade básica (0,41 g cm-3) e a densidade aparente (0,48 g cm-3) foram maiores em relação ao compensado e a porosidade foi menor. O inchamento residual (4,24%) e o aumento em inchamento em espessura (1,22%) foram maiores em relação ao compensado. Por apresentarem alta higroscopicidade, as aplicações dos painéis avaliados devem ser preferencialmente em ambientes sem contato com umidade.

A madeira é um dos os compostos orgânicos mais utilizados como matéria-prima no mundo. Suas características químicas, anatômicas e físicas variam sensivelmente mediante aos fatores ambientais. No Cerrado, os solos são naturalmente pobres e com estações secas prolongadas. O estudo das propriedades  da madeira produzida nesse bioma é relevante para compreensão das adaptações morfológicas no xilema secundário para sobrevivência da planta. Objetivou-se estudar as variações e correlações entre propriedades físicas e biométricas de fibras na madeira de Caryocar brasiliense Cambess. do cerrado de Minas Gerais. Coletou-se amostras de incremento do lenho de três árvores, utilizando-se trado de Pressler na altura de 1,30 m em relação ao solo. Determinou-se a densidade, umidade e dimensões das fibras da madeira no sentido medula-casca. Os parâmetros físicos variaram em função das árvores e da posição radial. As médias de densidade básica e umidade verde foram de 0,56 g/cm³ e 96,28%, respectivamente. A tendência observada nas propriedades físicas repetiu-se para os parâmetros biométricos das fibras. As médias de largura, espessura e comprimento de fibras foram 24,13 μm, 5,16 μm e 2,65 mm, respectivamente. O padrão de variação radial da madeira de pequi-do-cerrado indicou que ao se afastar da medula, a densidade básica e o comprimento das fibras são crescentes. Por outro lado, a umidade verde é decrescente. Para largura e espessura da parede celular das fibras não detectou-se tendências claras. Entre as árvores de C. brasiliense, constatou-se variação e correlação das propriedades físicas e particularidades anatômicas da madeira na mesma tipologia de cerrado.

Damages to ecosystems, due to the consumption of petroleum-based materials, can be mitigated with the use of biopolymers such as cellulose derivatives. The objective was to evaluate the influence of different proportions of cellulose micro/nanofibrils (MFC/NFC) on the properties of hydroxypropyl methyl cellulose (HPMC) films. Films were prepared using proportions of 0, 25, 50, 75 and 100% (w/w) of MFC/NFC of Pinus sp. in relation to HPMC. The physical, barrier, surface, optical, morphological and mechanical properties were evaluated. Data were analyzed with descriptive statistics, linear regression, principal component analysis and Pearson correlation. Solids content, basis weight and density values increased with higher MFC/NFC amount, while thickness and porosity were reduced. SEM images showed that films with more than 50% MFC/NFC had a more granular surface resulting in reduction of transparency from 80 to 65%. The water vapor penetration did not differ between films and the degradation in water was reduced from 40 to 5% as MFC/NFC was added. There were no differences for contact angle and wettability, but all films showed high resistance to fat penetration. Films with MFC/NFC contents between 75 and 100% showed higher values for tensile strength (50 to 65 MPa) and Young's modulus (6 to 10 MPa) and lower elongation at break (1 to 2%). The experimental results indicated that films with MFC/NFC contents above 50% have potential to be used as packaging material.

O objetivo desse trabalho foi avaliar a resistência natural da madeira de Hevea brasiliensis tratada com CCA, CCB e piretróide, em ensaios de deterioração de campo. Após 20 dias da aplicação dos preservantes, foi determinado o teor de extrativos totais, a massa específica básica, a porosidade e o potencial de resistência natural da madeira de Hevea brasiliensis. Os corpos de prova foram submetidos em dois ambientes: campo aberto, livre de vegetação rasteira e em floresta nativa. Periodicamente, a cada trinta dias, durante um ano, foram retirados seis corpos de prova por tratamento em cada ambiente estudado para determinação da massa seca residual. De acordo com os resultados, a madeira de Hevea brasiliensis apresentou um baixo teor de extrativos (<4%) e um baixo potencial de resistência natural. Apenas os tratamentos preservativos realizados com CCA e CCB apresentaram diferenças estatísticas significativas, sendo que no ambiente floresta as amostras apresentaram menor massa seca residual. O índice de deterioração no ambiente floresta chegou a 70% nas madeiras não tratadas e tratadas com piretróide e a 90% nas madeiras tratadas com CCA e CCB, indicando que o tratamento com esses dois últimos preservantes é eficaz para diminuir a deterioração da madeira de Hevea brasiliensis.