Fullerene single-wall nanotubes (SWNTs) were produced in yields of more than 70 percent by condensation of a laser-vaporized carbon-nickel-cobalt mixture at 1200degreesC. X-ray diffraction and electron microscopy showed that these SWNTs are nearly uniform in diameter and that they self-organize into "ropes," which consist of 100 to 500 SWNTs in a two-dimensional triangular lattice with a lattice constant of 17 angstroms. The x-ray form factor is consistent with that of uniformly charged cylinders 13.8 +/- 0.2 angstroms in diameter. The ropes were metallic, with a single-rope resistivity of <10(-4) ohm-centimeters at 300 kelvin. The uniformity of SWNT diameter is attributed to the efficient annealing of an initial fullerene tubelet kept open by a few metal atoms; the optimum diameter is determined by competition between the strain energy of curvature of the graphene sheet and the dangling-bond energy of the open edge, where growth occurs. These factors strongly favor the metallic (10,10) tube with C5v symmetry and an open edge stabilized by triple bonds.

Single-wall fullerene nanotubes were converted from nearly endless, highly tangled ropes into short, open-ended pipes that behave as individual macromolecules. Raw nanotube material was purified in large batches, and the ropes were cut into 100- to 300-nanometer lengths. The resulting pieces formed a stable colloidal suspension in water with the help of surfactants. These suspensions permit a variety of manipulations, such as sorting by length, derivatization, and tethering to gold surfaces.

No abstract