We report on a strong photoluminescence (PL) enhancement of monolayer MoS2 through defect engineering and oxygen bonding. Micro-PL and Raman images clearly reveal that the PL enhancement occurs at cracks/defects formed during high-temperature annealing. The PL enhancement at crack/defect sites could be as high as thousands of times after considering the laser spot size. The main reasons of such huge PL enhancement include the following: (1) the oxygen chemical adsorption induced heavy p doping and the conversion from trion to exciton; (2) the suppression of nonradiative recombination of excitons at defect sites, which was verified by low-temperature PL measurements. First-principle calculations reveal a strong binding energy of ∼2.395 eV for an oxygen molecule adsorbed on a S vacancy of MoS2. The chemically adsorbed oxygen also provides a much more effective charge transfer (0.997 electrons per O2) compared to physically adsorbed oxygen on an ideal MoS2 surface. We also demonstrate that the defect engineering and oxygen bonding could be easily realized by mild oxygen plasma irradiation. X-ray photoelectron spectroscopy further confirms the formation of Mo-O bonding. Our results provide a new route for modulating the optical properties of two-dimensional semiconductors. The strong and stable PL from defects sites of MoS2 may have promising applications in optoelectronic devices.

Semiconductors are the basis of many vital technologies such as electronics, computing, communications, optoelectronics, and sensing. Modern semiconductor technology can trace its origins to the invention of the point contact transistor in 1947. This demonstration paved the way for the development of discrete and integrated semiconductor devices and circuits that has helped to build a modern society where semiconductors are ubiquitous components of everyday life. A key property that determines the semiconductor electrical and optical properties is the bandgap. Beyond graphene, recently discovered two-dimensional (2D) materials possess semiconducting bandgaps ranging from the terahertz and mid-infrared in bilayer graphene and black phosphorus, visible in transition metal dichalcogenides, to the ultraviolet in hexagonal boron nitride. In particular, these 2D materials were demonstrated to exhibit highly tunable bandgaps, achieved via the control of layers number, heterostructuring, strain engineering, chemical doping, alloying, intercalation, substrate engineering, as well as an external electric field. We provide a review of the basic physical principles of these various techniques on the engineering of quasi-particle and optical bandgaps, their bandgap tunability, potentials and limitations in practical realization in future 2D device technologies.