No abstract

This study evaluated the influence of heat treatment (HT) of the silane on the microtensile bond strength of resin cement to a feldspathic ceramic. Ceramic (VITA VM7) and composite blocks (N=32) were divided into four groups (n=6 for bond test, n=2 for SEM) at random and subject to following sequence of conditioning: G1: HF 9.6%+Silane+Panavia F2.0, G2: HF 9.6%+Silane+HT+Panavia F2.0, G3: Silane+HT+Panavia F2.0, and G4: Silane+Panavia F2.0. HT was performed in an oven (100°C, 2 minutes). G1 (17.6±2.3 MPa) and G2 (19±3.2 MPa) showed significantly higher mean bond strength than those of G3 (9.1±2.8 MPa) and G4 (10.9±1.8 MPa). SEM analysis showed exclusively mixed failures. Silane HT did not increase the bond strength.

No abstract

The objective of this study was to evaluate the effect of the hydrofluoridric acid (HF) concentration and time of acid conditioning on bond strength of three glass ceramics to a resin cement. Thus, fifty blocks (10 mm x 5 mm x 2 mm) of each ceramic (LDCAD: IPS e.max CAD; LCAD: IPS Empress CAD and LDHP: IPS e.max Press) were made and embedded in acrylic resin. The surfaces were polished with sandpaper (#600, 800, 1000, and 1200 grits) and blocks were randomly divided into 15 groups (n = 10) according to the following factors: Concentration of HF (10% and 5%), conditioning time (20 s and 60 s) and ceramic (LDCAD, LDHP, and L). After conditioning, silane (Prosil / FGM) was applied and after 2 min, cylinders (Ø = 2 mm; h = 2 mm) of dual resin cement (AllCem / FGM) were made in the center of each block using a Teflon strip as matrix and light cured for 40 s (1,200 mW/cm 2 ). Then, the samples were thermocycled (10,000 cycles, 5/55°C, 30s) and submitted to the shear bond test (50 KgF, 0.5 mm/min). The data (MPa) were analyzed with 3-way ANOVA and Tukey's test (5%). Failure analysis was performed using a stereomicroscope (20x) and a scanning electron microscope (SEM). ANOVA revealed that the "concentration" factor (p = 0.01) and the interaction "acid concentration X ceramic" (p = 0.009) had a significant effect, however, the "ceramic" (p = 0.897) and "conditioning time" (p = 0.260) factors did not influence the results. The LDHP10% 60s (10.98 MPa) aA* group presented significantly higher bond strength than LDHP10% 20s (6.57 MPa) bA , LCAD5% 20s (6,90 ±3,5) aB and LDHP5% 60s (5.66 ± 2,9MPa) aA* groups (Tukey). Failure analysis revealed that 100% of specimens had mixed failure. In conclusion, etching with 5% HF for 20 seconds is recommended for lithium disilicate and leucite-reinforced CAD/CAM ceramics. However, for pressed lithium disilicate ceramic, 10% HF for 60 s showed significantly higher bond strength to resin cement.

This study evaluated the influence of different forms of heat treatment on a pre-hydrolyzed silane to improve the adhesion of phosphate monomer-based (MDP) resin cement to glass ceramic. Resin and feldspathic ceramic blocks (n=48, n=6 for bond test, n=2 for microscopy) were randomly divided into 6 groups and subject to surface treatments: G1: Hydrofluoric acid (HF) 9.6% for 20 s + Silane + MDP resin cement (Panavia F); G2: HF 9.6% for 20 s + Silane + Heat Treatment (oven) + Panavia F; G3: Silane + Heat Treatment (oven) + Panavia F; G4: HF 9.6% for 20 s + Silane + Heat Treatment (hot air) + Panavia F; G5: Silane + Heat Treatment (hot air) + Panavia F; G6: Silane + Panavia F. Microtensile bond strength (MTBS) test was performed using a universal testing machine (1 mm/min). After debonding, the substrate and adherent surfaces were analyzed using stereomicroscope and scanning electron microscope (SEM) to categorize the failure types. Data were analyzed statistically using two-way test ANOVA and Tukey's test (=0.05). Heat treatment of the silane containing MDP, with prior etching with HF (G2: 13.15 ± 0.89a; G4: 12.58 ± 1.03a) presented significantly higher bond strength values than the control group (G1: 9.16 ± 0.64b). The groups without prior etching (G3: 10.47 ± 0.70b; G5: 9.47 ± 0.32b) showed statistically similar bond strength values between them and the control group (G1). The silane application without prior etching and heat treatment resulted in the lowest mean bond strength (G6: 8.05 ± 0.37c). SEM analysis showed predominantly adhesive failures and EDS analysis showed common elements of spectra (Si, Na, Al, K, O, C) characterizing the microstructure of the glass-ceramic studied. Heat treatment of the pre-hydrolyzed silane containing MDP in an oven at 100 °C for 2 min or with hot air application at 50 ± 5 ºC for 1 min, was effective in increasing the bond strength values between the ceramic and resin cement containing MDP.