Nonradiative recombination losses originating from crystallographic distortions and issues occurring upon interface formation are detrimental for the photovoltaic performance of perovskite solar cells. Herein, we incorporated a series of carbamide molecules (urea, biuret, or triuret) consisting of both Lewis base (–NH2) and Lewis acid (–C=O) groups into the perovskite precursor to simultaneously eliminate the bulk and interface defects. Depending on the different coordination ability with perovskite component, the incorporated molecules can either modify crystallization dynamics allowing for large crystal growth at low temperature (60°C), associate with antisite or undercoordinated ions for defect passivation, or accumulate at the surface as an energy cascade layer to enhance charge transfer, respectively. Synergistic benefits of the above functions can be obtained by rationally optimizing additive combinations in an all-in-one deposition method. As a result, a champion efficiency of 21.6% with prolonged operational stability was achieved in an inverted MAPbI3 perovskite solar cell by combining biuret and triuret additives. The simplified all-in-one fabrication procedure, adaptable to different types of perovskites in terms of pure MAPbI3, mixed perovskite, and all-inorganic perovskite, provides a cost-efficient and reproducible way to obtain high-performance inverted perovskite solar cells.

Superhydrophobic films with excellent flexibility have been fabricated by combining the lift-up soft-lithography technique and chemical reduction of [Ag(NH 3 ) 2 ] + ions to Ag nanoparticles (NPs) on the surface of silica spheres which are patterned on the polydimethylsiloxane (PDMS) films. Scanning electron microscopy (SEM) images reveal the presence of raspberry-like hierarchical structures on the PDMS films. The influence of the amount of Ag NPs and the size of the silica spheres on the wettability of the soft films is investigated carefully. Because PDMS films are elastomeric materials, our superhydrophobic films offer great flexibility. The resulting films can be easily transferred from one substrate surface to another without destroying their superhydrophobicity. These flexible and superhydrophobic films can be used repeatedly to satisfy a wide range of applications.

The emerging inorganic CsPbI2Br perovskite is regarded as a promising candidate for future photovoltaics due to its superior photo-physical property and thermal stability, but it usually requires a high fabrication...