International audienceWe describe a procedure for the preparation of As-S-Se and As-Se-Te glasses with low contents of gas-forming impurities (hydrogen, oxygen, and carbon) via melting of extrapure-grade elements in an evacuated silica ampule and purification of the melt by chemical distillation. The impurity concentrations in the glasses thus prepared have been reduced to the following levels: hydrogen, <0.02; oxygen, 0.2; carbon, <0.02; silicon, <0.4 ppm by weight. Using the double-crucible method, we have fabricated glass fibers with various ratios of the core and cladding diameters (1: 25 to 9: 10), protected with a tetrafluoroethylene/1,1-difluoroethylene copolymer coating, which have an average bending strength of 0.5-1 GPa. The minimal optical losses are 150 dB/km at 6.6 μm in multimode As-Se-Te glass fibers and 60 dB/km at 4.8 μm in As-S-Se glass fibers. The effect of microinhomogeneities in the melt on the optical performance of arsenic sulfoselenide glass fibers fabricated by the double-crucible method is examined

Abstract:We have made and studied a set of the fiber lasers based on Ho-doped fiber with high concentration of the active ions. For the first time the spectral efficiency in a range of 2.02 -2.15 μm was determined. The highest output power of 4.2 W was detected at 2.1 μm with the efficiency slope of 34%. This value of the efficiency is highest for pure holmium-doped silica fibers.