To study the material based on the binary system Ti + Cu (50% atm), samples were produced from powders of commercially pure metals and additionally ground in a ball mill (final size about 12 µm) by spark plasma sintering. The following intermetallic phases were obtained in the materials: CuTi2, TiCu, and Ti3Cu4. The materials have a hardness of 363 and 385 HV (800 and 900 °C), a microhardness of 393 and 397 µHV, a density of 4.24 and 5.23 kg/m3, and resistance to corrosion in acids (weight gain + 0.002% after 24 h of testing according to ISO 16151 for a sample with 900 °C—the best result in comparison with steel 308, AA2024, CuA110Fe3Mn2). The hardness value varies due to the presence of pure metal agglomerates. The relationship between the temperature of spark plasma sintering and the characteristics of the material (material parameters improve with increasing temperature, segregation is reduced) is revealed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.