A Comparative Study on Strength Development, Chloride Diffusivity and Adiabatic Temperature Rise of Marine Concrete Depending on Binder Type

Abstract

Recently, in order to reduce a damage of chloride attack and hydration heat in marine concrete structures, blended cement in mixing the marine concrete is widely used. Long term strength development is distinct in concrete with blended cement and it also has excellent resistance to chloride attack and reduction of hydration heat. However, blended cement has a characteristic of relatively low compressive strength in early age of 28 days. On the other hand, a high level of compressive strength is required in the Standard Specification for marine concrete mix design. Such concrete mix design satisfying Standard Specification is effective to chloride attack but disadvantageous for hydration heat reduction due to large quantity of binder. In this study, the material properties of marine concrete considering water-binder ratio and binder type are experimentally investigated. Through the research results, compressive strength in blended cement at the age of 56 days is similar although it has smaller compressive strength at the age of 28 days compared with result of OPC (ordinary portland cement). Even though blended cement has a large water-binder ratio and small unit of binder content, chloride ion diffusion coefficient is still small and hydration heat is also found to be reduced. For meeting the required compressive strength in Standard Specification for marine concrete at 28 days, the increased unit content of binder is needed but the increased hydration heat is also expected.