This work introduces a new gradient fiber coating for microextraction of chlorobenzenes. Nanoclusters of organoclay-Cu(II) on a copper wire were fabricated by wireless electrofunctionalization. The resultant gradient coatings are more robust, and thermally and mechanically stable. Wireless electrofunctionalization was carried out in a bipolar cell under a constant deposition potential and using an ethanolic electrolyte solution containing stearic acid and montmorillonite. Stearic acid acts as an inexpensive and green coating while montmorillonite acts as a modifier to impart thermal stability. The gradient morphology of the nanoclusters was investigated by scanning electron microscopy, thermogravimetric analysis and energy dispersive X-ray spectroscopy. The coated wire was placed in a hollow needle and used for headspace in-tube microextraction (HS-ITME) of chlorobenzenes (CBs). Effects of various parameters affecting synthesis and extraction were optimized. Following extraction, the needles were directly inserted into the GC injector, and the CBs (chlorobenzene, 1,4-dichlorobenzene, 1,2-dichlorobenzene, 1,2,4-trichlorobenzene, 1,2,3,4-tetrachlorobenzene) were quantified by GC-MS. The limits of detection under optimized conditions range from 0.5 to 10 ng.L. The intra- and inter-day relative standard deviations (RSDs) (for n = 10, 5 respectively) using a single fiber are 6-10 and 10-15%, respectively. The fiber-to-fiber RSDs (for n = 3) is between 17 and 24%. The method was successfully applied to the extraction of CBs from real water samples, and relative recoveries are between 91 and 110%. Graphical abstract A gradient coating of organoclay-Cu nanoclusters was fabricated on a copper wire by wireless electrofunctionalization. The oxidation of copper takes place at the anodic pole (red) while dissolved oxygen in ethanol solution is reduced at the cathodic pole (blue).