Al-Doped ZnO/SiO2 Nano-glass Ceramic System: A New Composite System for Improvement in Thermal Stability and Mechanical Properties of Dental Resins

Abstract

This study aims to enhance dental resins' mechanical and thermal properties by reinforcing them with Al-doped ZnO/SiO2 nano-glass ceramic. The synthesis of the nano-glass ceramic involved the addition of Al-doped ZnO nano-powders to a diluted aqueous solution of liquid glass (25 mL) in ethanol (50 mL) at room temperature. The synthesized samples were characterized using TEM, EDS, FE-SEM, and XRD techniques. Various concentrations of the nano-glass ceramic (2, 5, 8, 10, and 15 wt.%) were then integrated with Bis-GMA and TEGDMA. The mechanical properties, including flexural strength (FS), compressive strength (CS), diameter tensile strength (DTS), and flexural modulus (FM), were evaluated. Thermal stability was assessed through TGA analysis, which indicated polymer degradation occurring between 300 and 450 °C. An increase in filler content correlated with enhanced thermal stability. The optimal mechanical properties were observed at a 7.5 wt.% filler content, showing significant improvements in FS (124.652 MPa), FM (9.87GPa), DTS (33.87 MPa), and CS (178.47 MPa).