An Analysis of the Mapping Relationship between Microstructure and Solidification Parameters during Aluminum Fused Coating

Zhao, Guangxi; Zhang, Jialei; Yang, Xianhai

doi:10.3390/met13091594

Cited by 1 publication

(1 citation statement)

References 32 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…As can be seen in figure 4, the microstructure morphology in the weld seam is determined by the relationship between the solidification rate and temperature gradient [43]. Therefore, it is possible to say that the weld metal grain structure formed after welding processes is affected by the solidification conditions controlled by the welding parameters [44].…”

Section: Weld Metal Nucleation Mechanismsmentioning

confidence: 99%

How to avoid solidification cracking in arc welding of aluminum alloys: a review on weld metal grain refinement approaches

Yolcu,

Kahraman

2023

Mater. Res. Express

View full text Add to dashboard Cite

Joining aluminum alloys with arc welding methods is frequently subject to literature and industrial applications. Although aluminum alloys have different difficulties in the arc welded process, the formation and elimination of solidification cracking defects is a more complex phenomenon. Since avoidance of this defect requires specific approaches and methods, special attempts and improvements have been studied frequently on this subject in recent years. Studies in the literature have clearly shown that this defect, which is often encountered in aluminum alloys, takes place along the grain boundaries. Therefore, the major approach to eliminate this defect is activating nucleation and decreasing the grain size. In this context, modification approaches in the literature, which are frequently used for arc welding of aluminum alloys, have been developed to use three different mechanisms including heterogeneous nucleation, dendrite fragmentation, and grain detachment. While it is aimed to increase heterogeneous nucleation by reinforcing filler metals with compounds in the inoculation approach; dendrite fragmentation and grain detachment are also aimed in the approaches where external effects and forces are used. Within the frame of references, it is also possible to review the external factors aiming to improve weld pool convection and thermal conditions under two headings, which are weld pool stirring and pulsed arc current approaches. The weld pool stirring approach also includes ultrasonic treatment and magnetic arc oscillation methods. In this study, solidification cracking defect that frequently occurs in the arc welding of aluminum alloys is explained fundamentally and the attempts to eliminate this defect are presented as a review paper in a comprehensive manner.

show abstract

Section: Weld Metal Nucleation Mechanismsmentioning

confidence: 99%