Annealing Effect on the Structural, Magnetic, Electrical, Optic Property, Nanomechanical, and Adhesive Characteristics of Co60Fe20Yb20 Thin Films on Glass Substrate
Abstract:In this study, X-ray diffraction (XRD) analysis showed the amorphous nature of the Co60Fe20Yb20 films deposited at room temperature (RT), 100 °C, and 200 °C. The body-centered cubic (BCC) CoFe (110) characteristic peak was visible at 44.7° after annealing films of 40 nm and 50 nm at 300 °C. The highest alternating current magnetic susceptibility (χac) value was 0.21 at 50 Hz in a 50 nm, and the lowest resistivity value was 1.02 (×10−2 Ω.cm) in a 50 nm. In terms of nano-indication measurement, the highest value… Show more
Set email alert for when this publication receives citations?
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.