Archives of Metallurgy and Materials

Abstract

In this research, Co-30 mass% Cr alloys were fabricated by a vacuum hot-press sintering process. Different amounts of submicron cobalt and chromium (the mean grain size is 800 and 700 nm, respectively) powders were mixed by ball milling. Furthermore, this study imposed various hot-press sintering temperatures (1100, 1150, 1200 and 1250°C) and pressures (20, 35 and 50 MPa), while maintaining the sintering time at 1 h, respectively. The experimental results show that the optimum parameters of hot-press sintered Co-30 mass% Cr alloys are 1150°C at 35 MPa for 1 h. Meanwhile, the sintered density reaches 7.92 g•cm -3 , the closed porosity decreases to 0.46%, and the hardness and transverse rupture strength (TRS) values increase to 77.2 HRA and 997.1 MPa, respectively. While the hot-press sintered Co-30 mass% Cr alloys at 1150°C and 20 MPa for 1 h, the electrical conductivity was slightly enhanced to 1.79 × 10 4 S•cm -1 , and the phase transformation (FCC → HCP) of cobalt displayed a slight effect on sintering behaviors of Co-30 mass% Cr alloys. All these results confirm that the mechanical and electrical properties of Co-30 mass% Cr alloys are effectively improved by using the hot-press sintering technique.