Attainment of high critical current in thick BaZrO3-doped YBa2Cu3O7 multilayer nanocomposite films

Abstract

High critical current (Ic) in high magnetic fields (B) with minimal variations with respect to the orientation of the B field is demanded by many applications such as high-field magnets for fusion systems. Motivated by this, this work studies 6 vol. % BaZrO3/YBa2Cu3O7 (BZO/YBCO) multilayer nanocomposite films by stacking two 10 nm thick Ca0.3Y0.7Ba2Cu3O7 (CaY-123) spacers with three BZO/YBCO layers of thickness varied from 50 to 330 nm to make the total film thickness of 150–1000 nm. The Ca diffusion from the spacers into BZO/YBCO was shown to dramatically enhance pinning efficiency of c-axis aligned BZO nanorods, which yields high and almost thickness independent critical current density (Jc) in the BZO/YBCO multilayer nanocomposite films. Remarkably, enhanced Jc was observed in these multilayer samples at a wide temperature range of 20–80 K and magnetic fields up to 9.0 T. In particular, the thicker BZO/YBCO multilayer films outperform their thinner counterparts in both higher value and less anisotropy of Jc at lower temperatures and higher fields. At 20 K and 9.0 T, Ic is up to 654 A/cm-width at B//c in the 6% multilayer (1000 nm) sample, which is close to 753 A/cm-width at B//ab due to the intrinsic pinning. This result illustrates the critical role of the Ca cation diffusion into the YBCO lattice in achieving high and isotropic pinning in thick BZO/YBCO multilayer films.